Discovery of mesoporous materials by Mobil researchers in 1992 opened a new field in catalytic applications. The materials designated as M41S family are MCM-41 with one-dimensional hexagonal structure, MCM-48 with three-dimensional cubic structure and MCM-51 with unstable lamellar structure. This family of materials have high surface areas up to 1500 m2/g, narrow pore size distributions with pore sizes varying from 20 to 100 Å / . These materials can be activated by incorporation of metals or active compounds into their structures.
In this study, copper and nickel incorporated MCM-41 type catalytic materials were synthesized via different methods namely, impregnation, high temperature and low temperature direct synthesis methods. The Cu-MCM-41, and Ni-MCM-41, as well as synthesized MCM-41 were characterized by using XRD, TEM, N2 sorption, SEM, XRF, EDS, AAS and TPR.
MCM-41 was synthesized with high temperature direct synthesis method. High surface area values up to 1400 m2/g of MCM-41 mesoporous materials were obtained with high pore volumes up to 1.17 cc/g.
Cu-MCM-41 type catalytic materials were synthesized with three different methods. Impregnation and high temperature direct synthesis methods gave better results than those of low temperature direct synthesis method. In impregnation, relatively high surface area values (730 m2/g) were obtained with Cu/Si mole ratio as high as 0.3 in the product. For the case of high temperature direct synthesis products, Cu/Si mole ratios as high as 0.26 were obtained with somewhat smaller surface areas (400 m2/g). Low temperature direct synthesis method is the least favorable method in metal loading.
Ni-MCM-41 type of catalytic materials were synthesized by impregnation and high temperature direct syntheses methods. Ni incorporation by high temperature direct synthesis method gave high surface area values (560-930 m2/g) having Ni/Si mole ratios of 0.12-0.28.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/3/12605788/index.pdf |
| Date | 01 February 2005 |
| Creators | Nalbant, Asli |
| Contributors | Dogu, Timur |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0018 seconds