Dissertação (mestrado)–Universidade de Brasília, Universidade UnB de Planaltina, Programa de Pós-Graduação em Ciência de Materiais, 2016. / Submitted by Fernanda Percia França (fernandafranca@bce.unb.br) on 2016-08-16T19:23:10Z
No. of bitstreams: 1
2016_LaudeniraVieiraMacielViana.pdf: 1583995 bytes, checksum: a6c0e832a2b9e04a514938f16f6d0cb4 (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2016-10-11T22:07:27Z (GMT) No. of bitstreams: 1
2016_LaudeniraVieiraMacielViana.pdf: 1583995 bytes, checksum: a6c0e832a2b9e04a514938f16f6d0cb4 (MD5) / Made available in DSpace on 2016-10-11T22:07:27Z (GMT). No. of bitstreams: 1
2016_LaudeniraVieiraMacielViana.pdf: 1583995 bytes, checksum: a6c0e832a2b9e04a514938f16f6d0cb4 (MD5) / Um dos aspectos mais importantes da ciência coloidal é atribuído à estabilidade dos sistemas coloidais, que para nanocolóides magnéticos, a densidade de carga, destaca-se por ser um dos parâmetros mais importantes para sua manutenção. Para determiná-la foi criada uma nova metodologia para sua medição, o denominado: Método Conjugado Potenciométrico e Condutimétrico (MPC). Este método utiliza de uma abordagem eletroquímica baseada na aplicação de titulação potenciométrica e condutimétrica simultâneas para sua medição. Para ferrofluidos do tipo EDL-MF, a origem do carregamento elétrico da superfície da nanopartícula está associada à transferência de prótons entre a superfície da partícula e o meio da dispersão. O presente trabalho tem como objetivo principal verificar a aplicabilidade deste método na determinação da densidade estrutural de carga da superfície de uma ferrita mista a base de nanopartículas do tipo core-shell ZnxCo1-x Fe2O4@ y-Fe2O3 sintetizadas pelo método de coprecipitação hidrotérmica de soluções, em dois diferentes meios alcalinos, obtendo com isso, amostras com dois tamanhos cristalinos distintos. Quanto ao estudo cristalográfico dos materiais foi utilizada a técnica de difração de raios X para determinar o tipo de estrutura cristalina, assim também como o seu tamanho médio. Com relação ao seu formato e polidispersão, foi utilizada a técnica de microscopia eletrônica de transmissão. __________________________________________________________________________________________________ ABSTRACT / The most important aspect on colloidal science and applicatinos is the so called colloidal stability. For charge colloids, as for example ferrofluids, the stability are directly related to the surface charge density. To determine it a new methodology was established, the so-called: The method combined potentiometric and conductimetric (MPC). This method uses an electrochemical approch based on simultaneous application of potenciometric and conductivimetric titrations. For electric double layred ferrofluids the surface charge density is associated to acid/base aqueous equilibria of the surfacic groups. This study aims to determine the applicability of MPC on the determination of the structural density surface charge of a core-shell type nanoparticles with formula ZnxCo1-x Fe2O4@ -Fe2O3 with two different crystal sizes. About the crystallographic study of the materials used was the technique of X-ray diffraction to determine the type of crystalline structure, so as their average size. With respect to its shape and polydispersity, the technique of transmission electron microscopy was used.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/21550 |
Date | 20 June 2016 |
Creators | Viana, Laudenira Vieira Maciel |
Contributors | Souza, Renata Aquino da Silva de |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds