A new tetragonal Heusler compound Mn1.4PtSn is synthesized. Crystal growth techniques that require growth directly from melt, such as Bridgman method, always result in microtwinned crystals. To get microtwin free crystals, another technique, flux method is employed, where growth can be done far below the melting point and martensitic transition temperature. The flux method results in successful large microtwin free crystals of Mn1.4PtSn.
The single-crystal diffraction is done on a small piece of single crystals of Mn1.4PtSn. From structural analysis, it is found out that the crystal structure of Mn1.4PtSn is the first tetragonal superstructure in the family of Heusler compounds. The superstructure reflections are clearly observed in the powder X-ray diffraction patterns.
Direction-dependent magnetic properties are measured. The compound is found to undergo two magnetic transitions. First, at 392 K, which corresponds to Curie temperature and second, at 170 K, which corresponds to the spin-reorientation transition temperature. The saturation magnetic moment at 2 K is very large of 4.7 µB/f.u.
The refinement of powder neutron diffraction reveals that in the temperature range of 170 to 392 K, the magnetic structure is collinear ferromagnet whereas below 170 K, it is a non-coplanar spin structure. The magnetic moment, obtained from refinement, is close to the saturation moment obtained from magnetization.
The electric transport properties are studied along the different crystallographic directions of the compound. The longitudinal resistivity measurement indicates that the compound is metallic and reveals the magnetic transitions at the same temperature as seen in the magnetization. An overall negative magnetoresistance of 3 percent is found. The Hall resistivity measurements reveal the presence of a large topological Hall resistivity (THE) of 0.9 µΩ cm and -0.1 µΩ cm for the magnetic field applied along [100] and [001], respectively. Two types of contributions in the THE for the field along [100] are seen. One that follows the quadratic form of longitudinal resistivity and second, that is independent of longitudinal resistivity. Anomalous Hall conductivity is found to be 250 and 165 Ω-1cm-1 for the field along [100] and [001], respectively. This value is close to the value obtained from theoretical calculations. The topological Hall conductivity is found to be approximately the same as its anomalous analog.
A new series of polycrystalline samples with iridium substitution at the place of platinum in Mn1.4PtSn are prepared. The structural characterization show the crystal structure of these compounds is the same as Mn1.4PtSn, therefore, they also possess the tetragonal superstructure form.
Magnetic properties, along with powder neutron diffraction data, reveal that the magnetic structure changes from out-of-plane ferromagnet to in-plane ferrimagnet with Ir-substitution. All the compounds are found to have metallic character. A large anomalous Hall conductivity of 405 Ω-1cm-1 is found for compound Mn1.4Pt0.7Ir0.3Sn.
Three new series of compounds are prepared as an attempt to fill the vacancies present in the crystal structure of Mn1.4PtSn with transition-metal elements cobalt, nickel, and copper. The tetragonal superstructure survives up to 0.2 cobalt addition, 0.4 nickel addition and 0.6 copper addition. Further addition of elements leads to transformation to the inverse cubic Heusler structure. The magnetic properties show that the compounds with tetragonal structure have spin-reorientation transition, which is absent in the compounds with cubic structure.
A new compound Mn1.7Pt0.8In is discovered. The single crystals are prepared by flux-method. Upon structural analysis from single-crystal refinement, it is found that the crystal structure is 3 × 3 × 3 superstructure of a Heusler structure and is so far the largest discovered in the Heusler family of compounds.
Two magnetic transitions are revealed in the magnetization measurements. First, at 330 K, which corresponds to Curie temperature and second, at 220 K, which corresponds to spin-reorientation transition. The magnetic moment is 0.4 µB/Mn at 2 K and 0.07 µB/Mn at 300 K. Such a low moment might be due to possible compensated ferrimagnetic structure. Therefore, the compound is a potential candidate for spintronics devices.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:72651 |
| Date | 30 October 2020 |
| Creators | Vir, Praveen |
| Contributors | Felser, Claudia, Inosov, Dmytro S., Technische Universität Dresden, Max Planck Institute for Chemical Physics of Solids, Dresden |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, doc-type:doctoralThesis, info:eu-repo/semantics/doctoralThesis, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0111 seconds