Electrochemical supercapacitors (ECs) attract significant attentions for their unique characteristics of high power density, good cycling capability and low cost. This dissertation will focus on fabrication of composite materials for electrodes and devices of ECs. A conceptually new colloidal approach to the fabrication of metal oxide – multiwalled carbon nanotube (MWCNT) composites is proposed. The heterocoagulation of positively charged oxide nanoparticles and negatively charged MWCNT allows the
fabrication of advanced nanocomposites with improved dispersion of individual components. The proof-of-principle was demonstrated by the fabrication of MnO2-MWCNT electrodes for ECs with excellent performance.
We proposed another novel concept based on electrostatic heterocoagulation of MnO2-MWCNT composites in aqueous environment. In this case, Benzyldimethylhexadecylammonium chloride (BAC) surfactant and caffeic acid (CA) were selected for adsorption and dispersion of MWCNT and MnO2, respectively, and this allowed the formation of stable aqueous suspensions of positively charged MWCNT and negatively charged MnO2. The asymmetric device showed high capacitance, high powerenergy
characteristics with enlarged voltage window of 1.8 V, good capacitance retention at high charge-discharge rates and cyclic stability. A novel capacitive material BiMn2O5 was firstly discovered and synthesized for ECs applications in our studies. The BiMn2O5 nanocrystals were prepared by a hydrothermal method. We demonstrated for the first time that BiMn2O5 – MWCNT composite can be used as a new active material for positive electrodes of ECs. The composite electrode
with high mass loading showed a capacitance of 6.0 F cm-2 (540 F cm-3) at a scan rate of 2 mV s-1 and excellent capacitive behavior at high scan rates. As-fabricated device showed good cyclic stability in a voltage window of 1.8 V with energy density of 13.0 Wh L-1 (9.0 Wh kg-1) and power density of 3.6 kW L-1 (2.5 kW kg-1).
We firstly discovered that Poly[1-[4-(3-carboxy-4 hydroxyphenylazo)benzenesulfonamido]-
1,2-ethanediyl, sodium salt] (PAZO) can be used as an universal dispersant for various materials and its thin film fabricated by electrophoretic deposition (EPD) exhibited photo-induced birefringence. Our new findings indicated that PAZO is good candidate for diverse materials dispersing because it contains diaromatic monomers with
salicylate ligands, which can provide multiple adsorption sites for efficient adsorption on particles and impart electrical charges to the particles. Additionally, the use of PAZO polymer offers the advantages of improved steric stabilization.
We discovered that Celestine blue (CB) can be developed as an efficient dispersing agent for the nanoparticles. We found that CB includes a catechol ligand, which can provide CB adsorption on inorganic nanoparticles. The relatively large size of the CB molecules is
beneficial for the electrosteric dispersion. The benefits of cathodic EPD for
nanotechnology were demonstrated by the formation of nanostructured MnO2 films on commercial high surface area current collectors for energy storage in ECs. / Thesis / Doctor of Philosophy (PhD)
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/19108 |
| Date | January 2016 |
| Creators | Liu, Yangshuai |
| Contributors | Zhitomirsky, Igor, Materials Science and Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0124 seconds