Orientador: Wolney Luiz Stolf / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-14T02:45:22Z (GMT). No. of bitstreams: 1
Duarte_RosangelaMarques_M.pdf: 1986447 bytes, checksum: 79b15a0794e37d92b9166336f4432e2e (MD5)
Previous issue date: 1992 / Resumo: A infiltração marginal em restaurações de cavidades classe I com compósito e base de cimento de ionômero de vidro foi observada neste estudo "in vitro". Cavidades classe I em 21 dentes humanos do grupo dos pré-molares foram preparadas. Os dentes foram divididos em 3 grupos,
sendo que as cavidades foram assim tratadas: No grupo A foram forradas com base de cimento de ionômero de vidro e restauradas com resina fluida e compósito. No grupo B foram forradas com base de cimento de ionômero de vidro, submetidas ao condicionamento ácido da base e das paredes de
esmalte. em seguida restauradas com resina fluida e compósito, e no grupo C foram forradas com uma base de cimento de ionômero de vidro, as paredes de esmalte foram submetidas ao condicionamento ácido e restauradas com resina fluida e compósito. Após restaurados, os dentes permaneceram por 24 horas à temperatura de 37°C e 100% de umidade relativa do ar. Em seguida foram submetidos a 100 ciclos térmicos com
temperatura variando entre 4 e 60°C. O selamento marginal foi medido usando avaliação da penetração do corante. Através de uma lupa est.ereoscópica (Carl Zeiss) os níveis de infiltração margi nal foram documentados e f'otografados. A análise dos resultados revelou que houve diferenças estatisticamente significativas quando se realizou o condicionamanto ácido do esmalte dentário, que demonstrou diminuir ou prevenir a inf'iltração marginal. O condicionamen~o ácido da base de cimento de ionômero de vidro, diferiu estatisticamente de quando não f'oi utilizado este tratamento. O uso de uma base de cimento de ionômero de vidro associado ao condicionamento ácido das paredes de esmalte impadiu a infiltração marginal em restaurações de cavidadas classe I com compósito / Abstract: The microleakage of composite resin/glass ionomer cement class I restorations was evaluated i n this "in vitro" study. A classic I cavity was prepared in 21 human pre-molares. The teeth were divided in three groups and the cavity preparations were treated as follows: in group A were
lined up with a glass ionomer cement base and restored with, unfilled resin and composite resin. In group B ware lined up with a glass ionomer cement base, submitted to enamel and base acid base acid etching treatment and restored with unfilled resin and composite resin, and in group C were lined up with a glass ionomer cement base submitted to enamel acid etching treatment and restored with unfilled resin and composite resin. After being restored the teeth ware stored for 24 hs at 37°C and 100% relative air humidity. In the following step they ware submited to 100 thermal cycles in water baths ranging in temperature from 4 to 60ºC. The marginal seal were measured using a dye penetration evaluation. Using a stereoscopic microscope the levels of microleakage Were recorded and photographed . The analysis of the results showed significant statistical difference when enamel acid etching treatmen'l was used, which proved to reduce or prevent miroleakage. The use of a base acid etching treatment differed statisticaly when was not used . The use of a glass ionomer cement base with acid etching the enamel walls prevented microleakage in composite/glass ionomer class I restorations / Mestrado / Materiais Dentarios / Mestre em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290275 |
| Date | 27 March 1992 |
| Creators | Duarte, Rosangela Marques |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Stolf, Wolney Luiz, 1937- |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | [92]f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0059 seconds