In recent years, there has been a considerable interest in organic semiconducting materials due to their potential to enable, amongst other things, low-cost flexible opto-electronic applications, such as large-area integrated circuitry boards, light-emitting diodes (OLEDs) and organic photovoltaics (OPVs). Promisingly, improved electronic performance and device structures have been realized with e.g. OLEDs entering the market and organic field-effect transistors (OFETs) reaching the performance of amorphous silicon devices; however, it would be too early to state that the field of organic semiconductors has witnessed the sought-after technological revolution. Initial progress in the field was mostly due to synthetic efforts in the form of enhanced regularity and purity of currently used materials, the creation of new molecular species, etc. In this thesis we show that the advancement of physico-chemical aspects – notably materials processing – and the realisation of increased order and control of the solid state structure is critical to realize the full intrinsic potential that organic semiconductors possess. We first investigated how the bulk charge-transport properties of the liquid-crystalline semiconductor poly(2,5-bis (3-dodecylthiophen-2-yl)thieno[3,2-b]thiophenes) (pBTTT-C12) can be enhanced by annealing in the mesophase. To this end, temperature treatment of a period of hours was necessary to realize good bulk charge transport in the out-of-plane directions. This behaviour is in strong contrast to in-plane charge transport as measured in thin-film field-effect structures, for which it was shown that annealing times of 10 min and less are often sufficient to enhance device performance. Our observation 4 may aid in future to optimize the use of pBTTT polymers in electronic devices, in which good bulk charge transport is required, such as OPVs. In the second part of thesis, we explored ink-jet printing of pBTTT-C12, in order to realize precise deposition of this material into pre-defined structures. In organic electronic applications this can, amongst other things, enable deposition of different semiconductors or reduction of the unwanted conduction pathways that often result in undesirable parasitic ‘cross-talk’, for instance, between pixels in display products. We demonstrate the integration of ink-jet printed transistors into unipolar digital logic gates that display the highest signal gain reported for unipolar-based logic gates. Finally, recognizing that a broad range of conjugated organic species fall in the category of “plastic crystals”, we explored the option to process this class of materials in the solid state. We find that solid-state compression moulding indeed can effectively be applied to a wide spectrum of organic small molecular and polymeric semiconductors without affecting adversely the intrinsic favourable electronic characteristics of these materials. To the contrary, we often observe significantly enhanced [bulk] charge transport and essentially identical field-effect transistor performance when compared with solution- or melt-processed equivalents. We thus illustrate that fabrication of functional organic structures does not necessitate the use of solution processing methods, which often require removal of 99 wt% or more of solvent, or precursor side-products, nor application of cumbersome vapour deposition technologies.
| Identifer | oai:union.ndltd.org:bl.uk/oai:ethos.bl.uk:535533 |
| Date | January 2010 |
| Creators | Baklar, Mohammed Adnan |
| Publisher | Queen Mary, University of London |
| Source Sets | Ethos UK |
| Detected Language | English |
| Type | Electronic Thesis or Dissertation |
| Source | http://qmro.qmul.ac.uk/xmlui/handle/123456789/1311 |
Page generated in 0.0016 seconds