Previous issue date: 2016-12-15 / O Silastic® MDX4-4210 é um dos materiais mais utilizados no mundo na confecção de próteses faciais devido às suas propriedades, contudo, ele apresenta algumas limitações, notadamente a que reduz o tempo de vida útil destas. O objetivo deste estudo foi avaliar a influência de pigmentos nas propriedades de um silicone para prótese facial submetido ao envelhecimento acelerado. Foram confeccionados 288 corpos de provas e divididos em três grupos: o Grupo Controle (GC) constituído por amostras do silicone Silastic® MDX4-4210 sem acréscimos de pigmento e os grupos experimentais G1 e G2. O Grupo 1 (G1), formado por amostras do silicone Silastic® MDX4-4210, pigmento com pó de maquiagem e, o Grupo 2 (G2), constituído por amostras de silicone com a incorporação da solução do pigmento de Urucum-Bixina (Bixa orellana L). Cada grupo foi constituído de 24 corpos de prova, sendo 09 unidades destinadas às caracterizações e 15 unidades aos ensaios mecânicos. Setenta e dois corpos de prova foram selecionados para serem avaliados antes do envelhecimento acelerado. Os 216 corpos de prova restantes, foram submetidos ao envelhecimento acelerado por exposição a ciclos de Ultravioleta, Temperatura e Umidade (UV/T/U) nos tempos de 120, 240 e 1000 horas. As amostras foram caracterizadas por meio de análise por Microscopia Ótica, Microscopia Eletrônica de Varredura, Espectroscopia na região do infravermelho com transformada de Fourier, Termogravimetria e os ensaios de Citotoxicidade, Sorção e Biodegradação Enzimática. Foram realizados os ensaios mecânicos (dureza Shore A, resistência ao rasgamento e à tração, módulo de elasticidade e alongamento a ruptura). Os dados obtidos foram analisados e obtidas as medidas estatísticas: média; mediana; desvio padrão. Os dados mostraram que não foram observadas mudanças significativas na cor ou textura em diferentes períodos de envelhecimento acelerado. Em geral, o material tornou-se mais resistente, mais duro, mais rígido e menos dúctil, conforme foi envelhecido, mas manteve uma deformação percentual superior a 100-120%. Apesar das alterações causadas pelo envelhecimento em suas propriedades mecânicas, o material envelhecido permaneceu suficientemente flexível e adequado para a aplicação proposta. Não houve diferença significativa entre as propriedades dos materiais pigmentados com maquiagem ou bixina. / Silastic® MDX4-4210 is one of materials most widely used in the world for facial prosthesis due to its properties, however, it has some limitations, that reduce its lifespan. The aim of this study is to evaluate the influence of pigments in the properties of a silicone for facial prosthesis subjected to accelerated aging. 288 samples were manufactured and divided in three groups: the control group (CG) consisting of Silastic® MDX4-4210 silicon samples without pigment and experimental groups G1 and G2. Group 1 (G1), consisted of Silastic® MDX4-4210 silicone samples, with makeup pigment powder and Group 2 (G2) consisting of silicone samples with the addition of a solution of Bixin (Bixa orellana L). Each group consisted of 24 specimens: 09 units for the characterizations and 15 units for mechanical tests. Seventy-two specimens were selected for further evaluation prior to accelerated aging. The 216 remaining specimens were subjected to accelerated aging by exposure to UV,temperature and humidity cycles (UV/T/U) for 120, 240 and 1000 hours. The samples were characterized by optical microscopy, scanning electron microscopy, Fourier transform infrared spectroscopy, thermogravimetry, Cytotoxicity assays, Sorption and Enzyme Biodegradation. Mechanical tests were also performed (Shore A hardness, tear resistance and tensile strength, elastic modulus and elongation to break). Data were analyzed and average, mean, median and standard deviation values were obtained. The data showed that no significant changes were observed in the color or texture in different periods of accelerated aging. In general, the material became tougher, stiffer, more rigid and less ductile, with aging but maintained a percentage deformation exceeding 100-120%. Despite the changes caused by aging changes the mechanical properties of the aged material remained suitable for the proposed application.There were no significant differences in the proprerties of the materials pigmented with either makeup or bixin.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1111 |
| Date | 06 July 2018 |
| Creators | HOLANDA, Geraldo Sávio Almeida. |
| Contributors | CARVALHO, Laura Hecker de., FOOK, Marcus Vinícius Lia., GOMES, Rodinei Medeiros., PINTO, Maria Roberta de Oliveira., BARBOSA, Rossemberg Cardoso., SILVA, Bartolomeu Jorge da. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds