Processo e caracterização de ligas Ti-Ni-Cu com efeito de memória de forma solidificadas rapidamente. / Process and characterization of Ti-Ni-Cu alloys with shape memory effect solidified rapidly. / Proceso y caracterización de aleaciones Ti-Ni-Cu con efecto de memoria de forma solidificadas rápidamente. / Processus et caractérisation d'alliages Ti-Ni-Cu avec effet de mémoire de forme rapidement solidifié. / Ti-Ni-Cu合金的工藝和特性表徵。

Description

Submitted by Johnny Rodrigues ([e-mail]) on 2018-04-06T20:54:52Z
No. of bitstreams: 1
GEORGE CARLOS DOS SANTOS ANSELMO - TESE PPG-CEMat 2014..pdf: 19735821 bytes, checksum: c92e61b342c27548f43bd01d30640a96 (MD5) / Made available in DSpace on 2018-04-06T20:54:52Z (GMT). No. of bitstreams: 1
GEORGE CARLOS DOS SANTOS ANSELMO - TESE PPG-CEMat 2014..pdf: 19735821 bytes, checksum: c92e61b342c27548f43bd01d30640a96 (MD5)
Previous issue date: 2014-08-29 / Ligas com efeito de memória de forma possuem grande potencial para
aplicações nos setores da robótica, automotivo, aeronáutico, medicina e na
produção de atuadores miniaturizados. O objetivo desse trabalho foi investigar e
desenvolver materiais com efeito de memória de forma (Shape Memory Effect -
SME) das ligas Ti-Ni-Cu na forma de fitas micrométricas produzidos por meio de
Melt Spinning. A metodologia utilizada para produção das ligas Ti-Ni-Cu foi via fusão
a plasma (Plasma Skull Push-Pull), e para fabricação de fitas utilizou-se a técnica de
solidificação rápida por injeção de metal líquido em volante de cobre nas
velocidades de 38 e 50 m/s, logos após as ligas e fitas Ti-Ni-Cu foram caracterizadas
por: DSC, SMRT, DRX, MEV. Inicialmente barras prismáticas da liga Ti-Ni50-x-Cux
(x=3,4,5,6,7%at.Cu) foram produzidas via fusão a plasma. Por meio solidificação
rápida obteve-se fitas com espessuras de 30 a 45 µm com a variação da velocidade
do volante de cobre de 38 e 50 m/s no Melt Spinning. Ensaios de DRX revelam à
presença da fase B19’ nas ligas brutas de fusão a temperatura ambiente. As ligas
apresentaram transformações de fase em único estágio B2↔B19`. As temperaturas
de transformação As das ligas Ti-Ni-Cu decrescem com o incremento de Cu. Concluise
que as temperaturas de transformação martensíticas (Ms) de fitas Ti-Ni-Cu
decrescem com a diminuição do tamanho de grão, e os valores de histerese e
entalpia decrescem quando altas taxas de super-resfriamento são alcançadas no
Melt Spinnig. / Alloys with shape memory effect have immense potential for applications in robotics,
automotive and aeronautics industry, medicine and in the production of miniaturized
actuators. The aim of this study was to investigate, develop and manufacture
materials with shape memory effect of Ti-Cu-Ni alloys in the form of micrometer tapes
produced by Melt Spinning. The methodology used for the production of Ti-Cu-Ni
alloys by fusion plasma (Plasma Skull Push-Pull), and manufacturing tapes used the
technique of rapid solidification injection of liquid metal into the copper wheel speeds
38 and 50 m/s. alloy and Ti-Ni-Cu ribbons were characterization by: DSC, SMRT,
XRD, SEM. Initially prismatic bars of Ti-Ni50-x-Cux (x = 3,4,5,6,7 at.Cu%) had been
produced by plasma fusion. With the rapid solidification is obtained tapes with
thicknesses between 30 to 45 µm with the variation of the speed of the wheel covers
38 and 50 m / s the melt spinning. XRD tests reveal the presence of the B19' in gross
phase alloy melting temperature. The alloys showed phase transformations in single
stage B2↔B19`. The transformation temperatures of the alloy Ti-Cu-Ni decrease with
the increase of Cu. We conclude that the temperatures of martensitic transformation
(Ms) of Ti-Ni-Cu ribbons decreases with decreasing grain size, and hysteresis values
and enthalpy decreases when high rates of super-cooling are achieved in Melt
Spinnig.

Links & Downloads

1. http://dspace.sti.ufcg.edu.br:8080/jspui/handle/riufcg/345
2. ANSELMO, George Carlos dos Santos. Processo e caracterização de ligas TI-NI-CU com efeito de memória de forma solidificadas rapidamente. 2014. 163f. (Tese de Doutorado), Programa de Pós-graduação em Ciência e Engenharia de Materiais, Centro de Ciências e Tecnologia, Universidade Federal de Campina Grande - Paraíba - Brasil, 2014.

Tags

Ciência e engenharia de Materiais.

Metalurgia – Engenharia de Materiais

Liga NiTiCu

Ligas com Memória de Forma

Melt Spinning

Alliages de mémoire de forme

Shape Memory Alloys

Ligas con Memoria de Forma

Transformações Martensíticas em Ligas

Martensitic Transformations in alloys

Additional Fields

Identifer	oai:union.ndltd.org:IBICT/oai:localhost:riufcg/345
Date	06 April 2018
Creators	ANSELMO, George Carlos dos Santos.
Contributors	CASTRO, Walman Benício de., ARAÚJO, Carlos José de., MACIEL, Theophilo Moura., CARVALHO, Laura Hecker de., AMORIM JÚNIOR, Wanderley Ferreira de., GONZALEZ, Cesar Henrique.
Publisher	Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT
Source Sets	IBICT Brazilian ETDs
Language	Portuguese
Detected Language	English
Type	info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis