Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2013. / Made available in DSpace on 2013-12-05T23:00:31Z (GMT). No. of bitstreams: 1
321423.pdf: 4114215 bytes, checksum: 29426d238ea097e10d8d5b386204ac3c (MD5)
Previous issue date: 2013 / Esta pesquisa analisou a condutividade elétrica como alternativa à obtenção de parâmetros de lixiviação de metais pesados em materiais cimentícios. Utilizaram-se corpos de prova cilíndricos de argamassas produzidas nos moldes recomendados para ensaios de resistência do cimento (NBR 7215:1997). O cimento escolhido foi do Tipo V e o agregado miúdo foi areia padrão. A contaminação das amostras se deu a partir de nitratos de metal pesado, por esta ser uma forma mais solúvel e susceptível à lixiviação. Foram utilizados nitratos de cromo, chumbo e zinco nas dosagens de 250 mg/kg, 500 mg/kg, 750 mg/kg e 1000 mg/kg. Os testes de lixiviação foram realizados de acordo com os procedimentos da norma holandesa NEN 7375:2004, na sua versão mais recente, no qual o extrato utilizado é a água deionizada. Trabalhou-se com tempos de cura variando de 28, 60 e 100 dias, para averiguação dessa influência sobre as taxas de liberação. As medidas da condutividade elétrica da solução lixiviada fazem parte dos procedimentos normalizados e servem para indicação da presença de elementos solubilizados. A condutividade elétrica da amostra monolítica foi tomada nos intervalos da troca do extrato a partir de eletrodos de cobre pressionados nas extremidades do corpo cilíndrico. Os equipamentos elétricos utilizados para leitura da condutividade do material consistiram de um gerador de tensão alternada e um medidor de corrente, posicionados em série. A tensão gerada foi fixada em 30 V e a frequência de 60 Hz, conforme a rede local. Os resultados mostraram existir semelhanças no comportamento à lixiviação das espécies e a condutividade elétrica, medida tanto na solução quanto no sólido. As correlações observadas permitiram a estimativa da concentração máxima de uma espécie qualquer disponível para liberação e, também, do tempo máximo decorrido até o seu esgotamento. Este procedimento pode substituir a realização dos ensaios prévios para determinação da disponibilidade de elementos susceptíveis à lixiviação. Os resultados parecem indicar não haver alteração na cinética de transporte das espécies iônicas ao longo do tempo e nem influência da concentração nesse movimento. <br> / Abstract : This research examined the electrical conductivity as an alternative to obtaining parameters of metal leaching in cementitious materials. Cylindrical specimens of mortars produced in the manner recommended for testing the compressive strength of cement were used (NBR 7215:1997). The chosen cement was Type V, and the fine aggregate was default standard sand. The contamination of the samples occurred from heavy metal nitrates, as this is more soluble and susceptible form to leaching. Nitrates of chromium, lead and zinc in doses of 250 mg/kg, 500 mg/kg, 750 mg/kg and 1000 mg/kg were used. The leaching tests were performed according to standard procedures of the Dutch NEN 7375:2004, in its latest version, in which the liquid solvent used is deionized water. The cure times ranged from 28, 60 and 100 days to investigate its influence on rates of release. The measurements of the electrical conductivity of the leach solution are part of the standard procedures and serve to indicate the presence of solubilized elements. The electrical conductivity of monolithic sample was taken at the intervals of exchange of the liquid solvent from pressed copper electrodes at the ends of the cylindrical specimens. The electrical equipment used for reading the conductivity of the material consisted of an alternating voltage generator and a current meter positioned in series. The generated voltage was set at 30 V and the frequency of 60 Hz, according to the mains. The results showed similarities in the leaching behavior of the species and the electrical conductivity, measured both in solution and in the solid. The observed correlations allowed the estimation of the maximum concentration of any species available for release and also the maximum time elapsed until its exhaustion. This procedure can replace the prior tests for determining the availability of elements susceptible to leaching. The results seem to indicate there is neither change in the kinetics of transport of ionic species over time nor influence of the concentration in this movement.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/107025 |
| Date | January 2013 |
| Creators | Vaillant, João Marcos Miranda |
| Contributors | Universidade Federal de Santa Catarina, Rocha, Janaíde Cavalcante, Cheriaf, Malik |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 246 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |