"Avaliação de cerâmicas odontológicas quanto à resistência de união com a dentina, por ensaio de tração, microdurezas Knoop e Vickers, rugosidade superficial e microscopia de força atômica" / Evaluation of dental ceramics regarding tensile bond strength to dentin, Knoop and Vickers’ microhardness, surface roughness and atomic force microscopy

Foram ensaiadas quatro cerâmicas VMK 95, Omega 900, IPS d. Sign e Cergogold. Os ensaios realizados foram: 1) resistência de união, por ensaio de tração, à dentina humana, de cones (6 x 3 x 5mm) de cerâmica, unidos por meio de cimentos fosfato de zinco, resinosos Rely X e Panávia F (n=10); 2) rugosidade pelos parâmetros Ra, Rt, Ry, Rz e Rp, de superfícies tratadas com ácido fluorídrico a 10% e polidas (n=10); 3) durezas Knoop e Vickers (n=4); 4) análise por microscopia de força atômica de superfícies polidas apenas (n=5). Os dados foram analisados pela análise de variância e testes de Tukey foram feitos quando necessário. A resistência de união com o fosfato de zinco e o parâmetro de rugosidade Ra foram analisados em separado, por apresentarem variâncias bem menores que as correspondentes aos demais agentes cimentantes e parâmetros. Os resultados mostraram que a resistência de união com o fosfato de zinco foi muito baixa (1,61 a 2,91MPa), nas condições dos ensaios. Com cimentos resinosos a resistência média variou de 16,61 a 18,47MPa. O cimento Rely X apresentou menor resistência em média, mas isto também depende da cerâmica.As rugosidades das superfícies tratadas com ácido fluorídrico a 10% foram bem maiores do que nas polidas. Nessas o parâmetro Ra variou de 2,15 a 4,26µm e os demais parâmetros de 10,99 a 21,93µm. Nas superfícies polidas o Ra variou de 0,53 a 0,84µm. Os demais parâmetros apresentaram médias de 2,01 a 5,23µm. A dureza Knoop variou de 418,9 a 493,8 kgf/mm2 e a Vickers de 492,5 a 572,2 kgf/mm2. Esta última apresentou valores maiores. A microscopia de força atômica permitiu visualizar irregularidades de superfícies. As principais conclusões foram: o cimento de fosfato de zinco, na condição do ensaio (por tração) apresentou resistência de união muito baixa; com os cimentos resinosos a resistência de união foi bem alta; as rugosidades foram muito altas após o tratamento superficial com ácido fluorídrico a 10%, mas, as polidas apresentaram valores bem baixos; as durezas Vickers fornecem valores maiores que a Knoop. / Four ceramics (VMK 95, Omega 900, IPS d.Sign and Cergogold) were tested regarding: 1) tensile bond strength to human dentin of ceramic cones (6 x 3 x 5mm), cemented with zinc phosphate, and resin cements, Rely X and Panávia F (n=10); 2) roughness by means of parameters Ra, Rt, Ry, Rz and Rp, of HF (10%) surface treated and polished surfaces (n=10); 3) Knoop and Vickers hardness (n=4); 4) atomic force microscopy; only of polished surfaces (n=5). Data were analyzed by ANOVA and when necessary were used Tukey’s tests. Tensile bond strength with zinc phosphate cement and Ra roughness parameter were analyzed separately because of their low variances when compared with those of resin cements and the other roughness parameter. Results showed that tensile bond strength of zinc phosphate was very low (1.61 to 2.91MPa) in this test condition (tensile test). Resin cements presented tensile bond strength at range 16.61 to 18.47MPa. Cement Rely X presented lower strength, but it depends also of ceramic. HF (10%) treated surfaces presented much higher roughness than polished ones. In HF (10%) treated surfaces parameter Ra ranged from 2.15 to 4.26µm and the other parameter ranged from 10.99 to 21.93µm. Roughness of polished surfaces Ra ranged from 0.53 to 0.84µm. Range of the other parameter was from 2.01 to 5.23µm. Knoop hardness ranged from 418.9 to 493.8 kgf/mm2 and Vicker’s from 492.5 to 572.2 kgf/mm2. This type presented higher values. Atomic force microscopy permited good vision of surface irregularities. Main conclusions were: zinc phosphate cement at test conditions (tensile) presented low bond strength; resin cements presented high tensile bond strength; surface treatment with HF (10%) led to high roughness but in polished one it was low; Vicker’s hardness presented higher values than Knoop one.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-04082006-095610
Date01 June 2006
CreatorsRicardo Ruiz Martuci
ContributorsAntonio Muench, Eduardo Bellini Ferreira, Estevao Tomomitsu Kimpara, Leonardo Eloy Rodrigues Filho, Mário Alexandre Coelho Sinhoreti
PublisherUniversidade de São Paulo, Odontologia (Materiais Dentários), USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0028 seconds