This dissertation presents work involving the manufacture and analytic modeling of microcantilever parts (length-width-thickness of roughly 500-100-10 microns). The manufacturing goals were to devise a means for and demonstrate repeatable production of microcantilevers from techniques not used in the integrated-circuit field, which are the exclusive means of current microcantilever production. The production of microcantilevers was achieved via a solvent casting approach and with injection molding, which produced parts from various thermoplastic polymeric materials (amorphous, semi-crystalline, fiber- and nanoclay-filled) in a repeatable fashion. Limits of the injection molding process in terms of the thinnest cantilevers possible were examined with 2 microns being the lower bound.
Subsets of the injection-molded parts were used in a variety of sensing applications, some results were successful (e.g., vapor-phase, resonance- and deflection-based sensing), while others showed poor results, likely due to experimental shortcomings (e.g., fluid-phase, deflection-based sensing). Additionally, microcantilever parts with integrated tips were injection-molded and showed to function at the same level as commercial, tipped, silicon-nitride parts when imaging an optical grating; this experimental work was the first demonstration of injection-molded parts for chemical sensing and force spectroscopy.
The scientific results were (i) the derivation of a length scale dependent bending stiffness and experimental evidence showing that such an effect was observed, (ii) the development of a new microcantilever experimental mode (surface stress monitoring via microcantilever bending resonant frequencies) and experimental validation of the technique, and (iii) a new method for determining microcantilever geometry based upon measurement of a bending, lateral, and torsional mode and experimental validation of the procedure.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/4895 |
| Date | 24 November 2004 |
| Creators | McFarland, Andrew W. |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Language | en_US |
| Detected Language | English |
| Type | Dissertation |
| Format | 10024923 bytes, application/pdf |
Page generated in 0.0019 seconds