Avaliação de materiais restauradores em cavidades retrogradas preparadas com pontas ultra-sonicas

Orientador : Francisco Jose de Souza Filho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-02T19:42:40Z (GMT). No. of bitstreams: 1
GondimJunior_Eudes_D.pdf: 7941631 bytes, checksum: a8b9f4b39b84e33266c5bdd50686a830 (MD5)
Previous issue date: 2002 / Resumo: O objetivo deste estudo foi comparar, usando réplicas de resina epóxica, a topografia de superfícies apicais de caninos humanos contento cavidades retrógradas preparadas com pontas ultra-sônicas antes e depois de seu preenchimento e acabamento com três diferentes técnicas. Também foi realizada uma avaliação quantitativa da capacidade de selamento marginal dessas obturações retrógradas. Oitenta e uma cavidades retrógradas preparadas em caninos humanos foram divididas em grupos de 27 cada. As cavidades foram preenchidas com Super-EBA, IRM, ou ProRoot-MTA e receberam um acabamento inicial com um brunidor de formato arredondado. Dezoito raízes de cada grupo receberam um acabamento final com brocas carbide de tungstênio 30 lâminas (9 raízes) ou com brocas de 28 mm Zekrya (9 raízes). Fotomicrografias de cada espécime obtidas com um microscópio eletrônico de varredura (MEV), antes e depois do preenchimento das cavidades retrógradas, foram comparadas através de um programa de análise de imagens. Após a análise da interface retrobturação/ dentina os espécimes foram preparados e imersos em uma solução de azul de metileno 2% por 12 horas. As raízes foram então trituradas e preparadas para análise em um espectrofotômetro de absorbância. Resultados obtidos mostraram que quando uma broca foi utilizada para um acabamento final nos materiais, uma área significativa (p < 0,05) de ranhuras marginais foi eliminada. A técnica de acabamento não afetou significativamente (p > 0,05) a incidência de fendas nos grupos retrobturados com MT A ou IRM. As obturações retrógradas feitas com Super EBA e IRM, e acabadas com um brunidor ou com brocas Zekrya apresentaram áreas calculadas das fendas significativamente (p < 0,05) maiores que as retrobturações feitas com MT A. Com relação à infiltração os resultados revelaram que o Pro Root MT A apresentou uma média de infiltração significativamente (p < 0,05) menor que retrobturações de Super-EBA e IRM. O fator técnica de acabamento não afetou significativamente (p > 0,05) a incidência de infiltração entre os materiais testados. O coeficiente de correção de Pearson indica que há uma associação positiva de 55,61 % entre as variáveis, ou seja, o acréscimo da quantidade de corante infiltrado está associado com o acréscimo da área de desadaptação das cavidades retrógradas / Abstract: The aim of this study was to compare, using epoxy resin replicas, the surface topography of root ends following ultrasonic preparation, and again after root-end fillings submitted to three different finishing techniques. A quantitatively evaluation of the sealing ability of Super-EBA, IRM and Pro Root MTA root-end fillings was also performed. Eighty-one ultrasonically root-end cavities prepared in human canines, were divided at random into three test groups of 27 each. The cavities were filled with Super-EBA, IRM, or ProRoot-MT A and finished by ball burnishing. Eighteen roots from each group received a final smoothing with either a 30-fluted tungsten carbide finishing bur, or a Zekrya carbide 28 mm bur. Scanning electron micrography (SEM) pictures of each sample were taken prior to and after root-end filling, and dentin/retrofilling interfaces inspected and compared with the aid of an image and analysis system. Samples were then prepared and immersed in 2% methylene blue dye solution for 12 hours. Roots were ground into a powder and prepared for analysis in an absorbency spectrophotometer. Results showed that when a finishing bur was used to finish the set materials, a significant (p < 0.05) area of marginal chipping was eliminated. The fishing technique did not significantly (p > 0.05) affect the incidence of gaps in groups retrofilled with MT A or IRM. Super EBA and IRM retrofillings finished with a ball burnisher or a Zekrya bur displayed a significantly (p < 0.05) larger calculated gap area than roots filled with MT A. In relation to microleakage the results revealed that Pro Root MT A displayed a significantly inferior mean dye microleakage (p < 0.05) than Super-EBA and IRM retrofillings. The finishing technique did not significantly (p > 0.05) affect the incidence of microleakage among the materials tested. The correlation coefficient of Pearson indicates that there is a positive, 55.61% association between the variables and this coefficient, that is, the increase of the quantity of infiltrated dye is associated with the increase of the root-end filling marginal disruption area / Doutorado / Endodontia / Doutor em Clínica Odontológica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289055
Date16 October 2002
CreatorsGondim Junior, Eudes
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Souza Filho, Francisco José de, 1950-2014, Cardoso, Rielson Jose Alves, Cardoso, Jose Leonardo, Bernabe, Pedro Felicio Estrada
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format171p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0025 seconds