Orientadores: Júlio Roberto Bartoli, Marcos Akira D'Ávila / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-20T09:53:53Z (GMT). No. of bitstreams: 1
Galvan_Danieli_M.pdf: 5419216 bytes, checksum: 3bbb69d4a9a4e73278d7ed9781b01c43 (MD5)
Previous issue date: 2012 / Resumo: O presente trabalho estudou a preparação e caracterização de híbridos de polímero-argila, tendo a poli(acrilonitrila-butadieno-estireno) (ABS) como matriz polimérica e duas argilas montmorilonitas organofílicas (MMTO) distintas e sua mistura binária 1:1 como fases dispersas. O objetivo foi avaliar os efeitos das variáveis: tipo de argila e processo nas propriedades físicas dos híbridos de ABS/MMTO. A seleção das argilas MMTO comerciais (Cloisite 30B e Cloisite 20A) baseou-se nas possíveis afinidades químicas de cada uma delas com as distintas fases do terpolímero ABS. Na preparação dos híbridos através do processo de intercalação no estado fundido, em extrusora com rosca-dupla co-rotacional, foi investigado o efeito do torque da rosca (ou tempo de residência na extrusora), na dispersão das argilas na matriz ABS. Os compostos obtidos foram caracterizados através de análises de difração de raios-X, termogravimetria, ensaios de tração uniaxial e resistência ao impacto, flamabilidade e análises reológicas do fundido em regime permanente e oscilatório em altas e baixas taxas de cisalhamento. A difração de raios-X indicou que os híbridos obtidos apresentavam estruturas intercaladas, que proporcionaram aumento nos módulos de elasticidade por tração e por cisalhamento (armazenamento e perda). As análises reológicas dos híbridos ABS mostram o surgimento de um caráter pseudo-sólido, em especial para os híbridos contendo a MMTO com maior afinidade química (Cloisite 30B) à fase SAN do terpolímero. Este comportamento indicaria uma provável dispersão em escala nanométrica da Cloisite 30B nos híbridos ABS, seja como único componente na fase dispersa ou na sua mistura binária com a Cloisite 20A. Este resultado caracterizaria os materiais obtidos como nanocompósitos. Melhorias significativas nas propriedades mecânicas de tração também foram verificadas nos híbridos a base de Cloisite 30B. Já os ensaios de rigidez ao impacto e as análises de estabilidade térmica não apresentaram resultados satisfatórios. Entretanto a adição de MMTO eliminou o gotejamento de material incandescente apresentado pelo ABS durante a queima (norma UL 94 HB). A utilização de um menor torque na rosca, ou seja, maior tempo de residência dos híbridos na extrusora, parece favorecer a dispersão/intercalação das argilas na matriz de ABS. Entretanto, o efeito deste fator foi confundido com variações na concentração nominal de argila / Abstract: This work studied the preparation and characterization of hybrids of polymer-clay, where the polymeric matrix was the poly(acrylonitrile-butadiene-styrene) (ABS) and two different organically modified montmorillonite (OMMT) and their mixture (1:1) were used as dispersed phase. The aim was evaluate the effect of kind of clay and process parameters on physical properties of ABS/OMMT hybrids. Two grades of commercial OMMT organoclay (Cloisite 20A and Cloisite 30B) were investigated, with distinct chemical affinities according to terpolymer phases, and a binary mixture of these clays. The hybrids were prepared by melt intercalation process, on a co-rotating twin-screw extruder, the effect of screw torque (or residence time on extruder) on clay dispersion in the polymeric matrix was investigated. The hybrids were characterized by analysis of X-ray diffraction, thermogravimetry, mechanical properties (uniaxial tensile and impact strength), flammability, and rheological analysis in steady and oscillatory states, at high and low shear rates. The X-ray diffractions indicated that the ABS hybrids present an intercalated structure, which improved the tensile elastic modulus and shear modulus (storage and loss). The rheological analysis of ABS hybrids shows the emergence of a pseudo-solid character, especially to the hybrids containing the OMMT with higher chemical affinity (Cloisite 30B) to SAN phase of the terpolymer. This behavior would indicate a probable nanometric scale dispersion of the Cloisite 30B on the hybrids of ABS, even in the single form or in a binary mixture, likely characterizing them as nanocomposites. Significant improvements in the tensile mechanical properties were also verified on the hybrids based on Cloisite 30B. Nevertheless the impact strength and thermal stability analysis did not show satisfactory results. The flammability test (UL 94 HB standard) of ABS hybrids showed a non-dripping effect of incandescent material during burning. The use of a lower screw torque, higher residence time of the hybrids on extruder, seems to favor clay dispersion/intercalation on the ABS matrix, however, the effect of this factor was confounded with some variations in the organoclay nominal content / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266780 |
| Date | 20 August 2018 |
| Creators | Galvan, Danieli |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, D'Avila, Marcos Akira, 1972-, Bartoli, Julio Roberto, 1954-, Fernandes, Elizabeth Grillo, Hui, Wang Shu |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 216 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0035 seconds