Double cantilever beam (DCB) specimens with distinct intermetallic microstructures and different geometries were fractured under different mode ratios of loading, ψ, to obtain critical strain energy release rate, Jc. The strain energy release rate at crack initiation, Jci, increased with phase angle, ψ, but remained unaffected by the joint geometry. However, the steady-state energy release rate, Jcs, increased with the solder layer thickness. Also, both the Jci and Jcs decreased with the thickness of the intermetallic compound layer.
Next, mode I and mixed-mode fracture tests were performed on discrete (l=2 mm and l=5 mm) solder joints arranged in a linear array between two copper bars to evaluate the J = Jci (ψ) failure criteria using finite element analysis. Failure loads of both the discrete joints and the joints in commercial electronic assemblies were predicted reasonably well using the Jci from the continuous DCBs. In addition, the mode-I fracture of the discrete joints was simulated with a cohesive zone model which predicted reasonably well not only the fracture loads but also the overall load-displacement behavior of the specimen. Additionally, the Jci calculated from FEA were verified estimated from measured crack opening displacements in both the continuous and discrete joints.
Finally, the pad-crater fracture mode of solder joints was characterized in terms of the Jci measured at various mode ratios, ψ. Specimens were prepared from lead-free chip scale package-PCB assemblies and fractured at low and high loading rates in various bending configurations to generate a range of mode ratios. The specimens tested at low loading rates all failed by pad cratering, while the ones tested at higher loading rates fractured in the brittle intermetallic layer of the solder. The Jci of pad cratering increased with the phase angle, ψ, but was independent of surface finish and reflow profile. The generality of the J =Jci(ψ) failure criterion to predict pad cratering fracture was then demonstrated by predicting the fracture loads of single lap-shear specimens made from the same assemblies.
| Identifer | oai:union.ndltd.org:TORONTO/oai:tspace.library.utoronto.ca:1807/29822 |
| Date | 31 August 2011 |
| Creators | Nadimpalli, Siva |
| Contributors | Spelt, Jan K. |
| Source Sets | University of Toronto |
| Language | en_ca |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0027 seconds