Previous issue date: 2015-06-15 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior (CAPES) / Os materiais cer?micos a base de alumina t?m sido bastante utilizados em componentes estruturais principalmente pelo fato de possuir propriedades como alta dureza, in?rcia qu?mica e boa resist?ncia ao desgaste, entretanto, sua baixa tenacidade ? um fator que compromete seu uso em diversas outras aplica??es, tendo a adi??o de n?quel como uma poss?vel solu??o para este problema, nesse contexto, esse trabalho tem como objetivo estudar a adi??o de n?quel em alumina utilizando a rota da metalurgia do p?. O percentual de n?quel adicionado variou em 2, 4 e 6% p e para cada composi??o foi realizada moagem de alta energia em moinho planet?rio por 2, 4, 9 e 16h. Posteriormente as amostras foram compactadas a 300 MPa e sinterizadas em forno ? v?cuo a 1400?C por 2h. As amostras foram caracterizadas quanto as propriedades f?sicas e mec?nicas observando-se no geral uma melhora na sinterabilidade com o aumento do tempo de moagem e teor de n?quel, com diminui??o e homogeneiza??o da porosidade e aumento da dureza, al?m de densidades acima de 80% da te?rica, observou-se tamb?m uma disparidade no tempo de moagem de 4 horas, onde se alcan?ou os maiores valores de dureza (2% de n?quel), de 1068,7 +/- 32,6 HV e densidade cerca de 99% da te?rica / Ceramic materials alumina basis have been widely used in structural components, mainly because owning properties such as high hardness, chemical inertness and good wear resistance, however, the low toughness is a factor that compromises its use in many other applications, featuring the addition of nickel as a possible solution to this problem, in this context, this work aims to study the addition of nickel alumina using the route of powder metallurgy processing of the material. The percentage of nickel were added 2, 4 and 6 wt%; and each composition to high energy milling in a planetary mill was performed for 2, 4, 9 and 16h. Subsequently, the samples were compacted at 300 MPa and sintered in a vacuum oven at 1400?C for 2h. The samples were characterized as the physical and mechanical properties, observing, in general, an improvement in sinterability of the material with increasing grinding time and nickel content, and mixing with a decrease of porosity and increase of hardness, density values above 80% of theoretical were obtained. The milling time of 4 hours and addition of 2% nickel, particularly if achieved higher hardness (HV 1068.7 +/- 32.6) and density of about 99% theoretical density.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/21025 |
| Date | 15 June 2015 |
| Creators | Oliveira, Arthur Gabriel Ferreira de |
| Contributors | 05012180410, http://lattes.cnpq.br/9858094266525225, Silva, Ariadne de Souza, 00735940401, http://lattes.cnpq.br/5623381698478389, Oliveira, Leiliane Alves de, 01081015411, http://lattes.cnpq.br/7082478793734403, Machado, Tercio Graciano, 44475039487, http://lattes.cnpq.br/9611851267523626, Gomes, Uilame Umbelino |
| Publisher | Universidade Federal do Rio Grande do Norte, PROGRAMA DE P?S-GRADUA??O EM CI?NCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds