Previous issue date: 2006-06-14 / This work reports the influence of the poly (ethylene terephthalate) textile surface modification by plasmas of O2 and mixtures (N2 + O2), on their physical and chemical properties. The treatment was carried out in a vacuum chamber. Some parameters remained constant during all treatment, such as: Voltage 470 V; Pressure 1,250 Mbar; Current: 0, 10 A and gas flow: 10 cm3/min. Other parameters, such as working gas composition and treatment time, were modified as the following: to the O2 plasma modified samples only the treatment time was changed (10, 20, 30, 40, 50 and 60 minutes). To the plasma with O2 and N2 only the chemical concentrations were changed. Through Capillary tests (vertical) an increase in textile wettability was observed as well as its influence on aging time and its consequence on wettability. The surface functional groups created after plasma treatments were investigated using X-ray Photoelectron Spectroscopy (XPS). The surface topography was examined by scanning electron microscope (SEM) / Neste trabalho, investigou-se a influ?ncia do tratamento superficial a plasma utilizando como gases de trabalho o oxig?nio e uma mistura de nitrog?nio + oxig?nio, sobre as propriedades f?sicas e qu?micas do tecido 100% Poli?ster. O tratamento foi realizado em uma c?mara contendo os gases de trabalho sob baixa press?o (~ 1 mbar) mantendo-se constante durante todo ensaio alguns par?metros do plasma, tais como, voltagem: 470 V; press?o: 1,250 mbar; corrente: 0,10 A e fluxo de g?s: 10 cm3/min. Para os tratamentos com plasma de oxig?nio puro utilizaram-se diferentes tempos de tratamento: 10, 20, 30, 40, 50 e 60 minutos. Para os tratamentos com plasma de N2 O2, fixou-se o tempo de tratamento em 10 minutos e variaram-se as concentra??es de N2 entre 10% - 90%. Atrav?s do teste de capilaridade (arraste vertical) foi observada a melhora na hidrofilidade do tecido, bem como a influ?ncia da a??o do tempo sobre o tratamento superficial e sua conseq??ncia frente ? molhabilidade. A cria??o de grupos funcionais na camada superficial foi investigada por espectroscopia de fotoel?trons excitados por raios-X (XPS). A topografia foi observada por microscopia de varredura eletr?nica (MEV)
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/12836 |
| Date | 14 June 2006 |
| Creators | Feitor, Michelle Cequeira |
| Contributors | CPF:09621199468, http://lattes.cnpq.br/7441669258580942, Fontana, Luis C?sar, CPF:61822957915, http://lattes.cnpq.br/9403290679198474, Pereira, M?rcia Rodrigues, CPF:83115951787, http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4788568T8, Bezerra, Cl?vis de Medeiros, Alves J?nior, Clodomiro |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Ci?ncia e Engenharia de Materiais, UFRN, BR, Processamento de Materiais a partir do P?; Pol?meros e Comp?sitos; Processamento de Materiais a part |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds