Previous issue date: 2014-11-03 / Capes / Mulita sintética é um material que tem recebido atenção especial devido as
suas propriedades químicas, físicas e mecânicas, que estão correlacionadas
com o método de síntese utilizado. O método sol-gel destaca-se frente aos
outros métodos químicos devido a possibilidade de obtenção de materiais com
elevado grau de pureza e baixas temperaturas de síntese. Sendo assim, este
trabalho tem por objetivo a análise da influência do solvente na obtenção de
mulita por meio de diferentes rotas sol-gel: rota Pechini, rota por gelificação
lenta e rota por gelificação rápida. Para cada rota estudada foi analisada a
influência dos solventes água, álcool etílico, álcool isopropílico e
tetrahidrofurano (THF), na obtenção da mulita. As amostras foram
caracterizadas por difração de raios X (DRX), análise térmica (TG e ATD),
adsorção por nitrogênio (BET), microscopia eletrônica de varredura (MEV) e
microscopia eletrônica de transmissão (MET). Os resultados mostraram a
influência das diferentes rotas e solventes na obtenção da mulita. Através da
Rota Pechini a fase mulita foi formada quando se usou apenas o álcool etílico
como solvente. Na gelificação lenta e rápida todos os solventes estudados
cristalizaram mulita dependendo do controle de outras variáveis do processo,
tais como: solvente utilizado, concentração da solução, temperatura, etc.
Comparativamente, a Rota Pechini obteve mulita com menor cristalinidade do
que todas as demais rotas, possuindo a maior área superficial e a morfologia
mais porosa. Na gelificação lenta a mulita foi sintetizada em praticamente todas
as condições de síntese e com todos os solventes, porém, o uso dos alcoóis
como solvente proporcionou a obtenção das amostras mais cristalinas, com
elevada reatividade, possuindo as menores áreas de superfície, com uma
morfologia formada por agregados e partículas individualizadas. Na gelificação
rápida a baixa concentração da solução juntamente com o uso dos alcoóis
como solvente, foi a condição mais indicada. Porém, esta rota apresentou mais
heterogeneidades, possuindo menor cristalinidade, e com isso maiores áreas
superficias, em relação a gelificação lenta, sendo a morfologia formada por
grandes agregados e considerável quantidade de fase vítrea. / Mullite is a synthetic material that has received particular attention due to their
chemical, physical and mechanical properties, which are correlated with the
synthesis method used. The sol-gel method stands out compared to the other
chemical methods due to the possibility of obtaining materials with high purity
and low temperatures for synthesis. Therefore, this study aims to analyze the
influence of the solvent to obtain mullite via different sol-gel routes: Pechini
route, route by route by slow gelation and rapid gelation. Studied for each route
was examined the influence of the solvents water, ethyl alcohol, isopropyl
alcohol and tetrahydrofuran (THF), to obtain mullite. The samples were
characterized by X-ray diffraction (XRD), thermal analysis (TG and DTA),
nitrogen adsorption (BET), scanning electron microscopy (SEM) and
transmission electron microscopy (TEM). The results showed the influence of
different routes and solvents in obtaining the mullite. By the Pechini Route
mullite was formed when it used only ethanol as a solvent. In the slow and fast
gelling all solvents studied crystallized mullite depending on the control of other
process variables, such as solvent used, the solution concentration,
temperature, etc. Comparatively, the Pechini Route mullite obtained with lower
crystallinity than all other routes, has the largest surface area and a more
porous morphology. In the slow gelation mullite was synthesized in almost all
synthesis conditions and all solvents, however, the use of alcohols as solvent
gave obtaining the most crystalline samples with high reactivity, having the
smaller surface areas, with a morphology formed by aggregates and individual
particles. In the fast gelation of the solution at low concentration with the use of
alcohols as solvent, was indicated condition. However, this route showed more
heterogeneities having lower crystallinity, and thus superficias larger areas, for
the slow gelation morphology being formed by large aggregates and
considerable amount of glassy phase.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/170 |
| Date | 01 December 2017 |
| Creators | BRAGA , Aluska do Nascimento Simões. |
| Contributors | MENEZES , Romualdo Rodrigues., LIRA, Hélio de Lucena., NEVES, Gelmires de Araújo., SANTANA, Lisiane Navarro de Lima., SILVA, José Valmir da., CARTAXO, Juliana de Melo. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds