Previous issue date: 2014-08-29 / The purpose of this research was to prepare biocompatible and absorbable polymeric composites films of chitosan and PLGA with PPy nanofibers for application in peripheral nerve regeneration. The QT and PLGA films were prepared by solvent evaporation technique and PPy was synthesized by chemical oxidative polymerization using PTSA as dopant agent. In order to check the degradation time of the films, were performed a in vitro degradation tests. The nanofibers and PPy films produced were characterized by Scanning Electron Microscopy (SEM), Infrared Spectroscopy Fourier Transform (ATR / FT-IR), Thermal Gravimetric Analysis (TGA), Atomic Force Microscopy (AFM), X-ray Computed Microtomography (μCT), Electrical Impedance Spectroscopy (EIS) and Electrometer. The PPy nanofibers synthesized showed a conductivity of 8x10-4 S/cm and the PLGA - PPy film produced showed a conductivity of 1x10-7 S/cm. The addition of PPy nanofibers accelerated the degradation of the composite films when compared to the array and significantly changed the morphology of the films of PLGA and QT, forming frameworks that may promote nerve regeneration. / A finalidade desta pesquisa foi preparar filmes biocompat?veis e reabsorv?eis de comp?sitos polim?ricos de quitosana (QT) e poli (?cido l?ticoco- ?cido glic?lico) (PLGA) com nanofibras de polipirrol (PPy) para aplica??o na regenera??o de nervos perif?ricos. Os filmes de QT e PLGA foram preparados pelo m?todo de evapora??o do solvente e a polimeriza??o do PPy foi realizada via polimeriza??o qu?mica oxidativa usando APTS como agente dopante. Com o intuito de verificar o tempo de degrada??o dos filmes, foram realizados ensaios de degrada??o in vitro. As nanofibras de PPy e os filmes produzidos foram caracterizados por Microscopia Eletr?nica de Varredura (MEV), Espectroscopia no Infravermelho por Transformada de Fourier (ATR/FT-IR), An?lise termogravim?trica (TGA), Microscopia de For?a At?mica (AFM), Microtomografia Computadorizada de Raios X (Micro CT), Espectroscopia de Imped?ncia El?trica (EIE) e Eletr?metro. As nanofibras de PPy sintetizadas apresentaram uma condutividade 8x10-4 S/cm e o filme de PLGA-PPy apresentou uma condutividade de 1x10-7 S/cm. A adi??o das nanofibras de PPy acelerou a degrada??o dos filmes comp?sitos em rela??o a matriz e modificou significativamente a morfologia dos filmes de PLGA e QT formando arcabou?os que podem vir a favorecer a regenera??o nervosa.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.pucrs.br:tede/3271 |
| Date | 29 August 2014 |
| Creators | Pilar, Fabiana Dias |
| Contributors | Basso, Nara Regina de Souza |
| Publisher | Pontif?cia Universidade Cat?lica do Rio Grande do Sul, Programa de P?s-Gradua??o em Engenharia e Tecnologia de Materiais, PUCRS, BR, Faculdade de Engenharia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS, instname:Pontifícia Universidade Católica do Rio Grande do Sul, instacron:PUC_RS |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -7432719344215120122, 500, 600, -655770572761439785 |
Page generated in 0.0016 seconds