Orientador: Ana Rita Morales / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-16T01:54:01Z (GMT). No. of bitstreams: 1
Coelho_PauloHenriquedaSilvaLeite_M.pdf: 3567481 bytes, checksum: e65ba429faa53dd840da6f11f7155c0e (MD5)
Previous issue date: 2010 / Resumo: O trabalho descreve a obtenção de nanocompósitos de polietileno de baixa densidade, poliamida 6, polietileno enxertado com anidrido maleico e montmorilonita organofilicamente modificada com o objetivo de estudar o efeito de compatibilização da argila organofílica nas blendas de polietileno e poliamida. Os compostos foram preparados pelo método de intercalação do fundido em extrusora dupla-rosca e os corpos de prova, obtidos por injeção, foram caracterizados por análise térmica dinâmico-mecânica, microscopia eletrônica de varredura, difração de raios-X, microscopia eletrônica de transmissão, calorimetria exploratória diferencial, análise termogravimétrica e teste mecânicos de resistência a tração e ao impacto. As análises térmicas revelaram uma ligeira queda da estabilidade térmica associada ao efeito de degradação do modificador encontrado na argila; o aparecimento de um novo pico de fusão nas curvas de DSC dos nanocompósitos foi associado à formação de uma nova fase cristalina na poliamida 6, causado pela presença da argila. As análises morfológicas revelaram uma adequada homogeneidade nos nanocompósitos e uma redução dos tamanhos dos domínios das duas fases da blenda, de forma que nenhum aglomerado foi observado, o que mostra que houve uma boa dispersão da argila na matriz. As análises estruturais confirmaram esta boa dispersão através da microscopia eletrônica de transmissão (MET) e da difração de raios-X (DRX), que revelaram que a argila teve suas camadas parcialmente intercaladas e/ou esfoliadas em todos os nanocompósitos estudados, e que esta estrutura encontrada proporcionou uma melhora significativa nas propriedades mecânicas dos compostos / Abstract: This work describes the behavior of nanocomposites of polyamide 6 (PA6), low density polyethylene (LDPE) and an organophilic montmorillonite. The compatibilization effect of the orgalophilic clay was studied with and without the presence of a maleic anhydride grafted polyethylene (PE-g-MA). The nanocomposites were prepared by melt intercalation on a twin screw extruder. The samples were prepared by injection molding, and characterized using scanning electron microscopy (SEM), wide-angle X-diffraction (WAXD), dynamic mechanical analysis (DMA), transmission electron microscopy (TEM) and differential scanning calorimeter (DSC). Mechanical properties as tensile strength and impact strength were also evaluated. The thermal analysis showed a slight decrease in thermal stability that was associated with the effect of degradation of the modifier of the clay; the emergence a new melting peak for the Polyamide 6 associated to a new crystalline phase due the clay nucleation effect. The morphologic analysis showed two phases for all systems but a reduction on the particle dimension due the presence of the clay, with low differences by the use of the compatibilizer. Structural analysis confirmed by transmission electron microscopy (TEM) and X-ray diffraction (XRD), which had its clay layers extensive exfoliated, with some small degree of intercalation nanocomposites at all, and that this structure has provided a significant improvement in mechanical properties of compounds / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266910 |
Date | 16 August 2018 |
Creators | Coelho, Paulo Henrique da Silva Leite, 1985- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Morales, Ana Rita, 1958-, Bettini, Silvia Helena Prado, Bartoli, Julio Roberto |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 144 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds