Selective 3D Submicron Glass Imprint Heads Fabrication by FIB for UV Cure

Focused Ion Beam (FIB) has several advantages such as high sensitivity, high material removal rates, low forward scattering and directing fabrication. Without any etched mask, processing time can be reduced. Pyrex glass etched by FIB is used for fast fabrication of 3-D submicron structure mold. In this study, glass is used as substrate. The UV-cured resin that spin-coated onto a mold has 3-D structure patterns. 3-D structure patterns are transferred on the plate to investigate the effects of parameters of UV cured, pressure and exposure time on the occurrence of defects. The relationship of these processing parameters for the imprinting process is also realized. Besides, the material property of UV-cured resin is investigated. UV-Cured resin is investigated by thermogravimetric Analysis (TGA) to measure the degradation temperature (Td). The hardness and modulus of UV-Cured resin was measured by nanoindentation to realize deformed ability of material for the imprinting process. Moreover, the contact angle of Pyrex glass is measured to investigate its surface quality for the imprint process.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0214107-171701
Date14 February 2007
CreatorsYang, Shih-yi
ContributorsChien-Hsiang Chao, Cheng-Tang Pan, Shyue-Jian Wu
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageCholon
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0214107-171701
Rightsnot_available, Copyright information available at source archive

Page generated in 0.0023 seconds