Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2013. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2014-05-29T13:53:33Z
No. of bitstreams: 1
2013_LuimarNogueiraCorreaFilho.pdf: 4325141 bytes, checksum: 6b70588cf62bfeeb4f43d41292196952 (MD5) / Approved for entry into archive by Guimaraes Jacqueline(jacqueline.guimaraes@bce.unb.br) on 2014-05-30T11:51:13Z (GMT) No. of bitstreams: 1
2013_LuimarNogueiraCorreaFilho.pdf: 4325141 bytes, checksum: 6b70588cf62bfeeb4f43d41292196952 (MD5) / Made available in DSpace on 2014-05-30T11:51:13Z (GMT). No. of bitstreams: 1
2013_LuimarNogueiraCorreaFilho.pdf: 4325141 bytes, checksum: 6b70588cf62bfeeb4f43d41292196952 (MD5) / Com o surgimento de novas tecnologias, novos materias são necessários para que esta evolução aconteça, este é o caso das ligas com memória de forma, em particular ligas de Níquel Titânio (NiTi). Uma liga metálica que possui propriedades singulares como amortecimento, elasticidade, recuperação da
geometria inicial, sendo utilizada em diversos ramos como medicina, odontologia,
aeronáutica, indústria automotiva, construção civil e etc. No setor elétrico,
especificamente em linhas de transmissão de energia elétrica, as quais sofrem ação
dos ventos e após determinado tempo falham por fadiga nos pontos de fixação, para
evitar tal acontecimento, são utilizados absorvedores dinâmicos de vibração que
reduzem ou eliminam as vibrações geradas pela ação dos ventos absorvendo energia. Neste trabalho foi estudada a influência do tratamento térmico nas propriedades mecânicas e térmicas de uma liga NiTi pseudoelástica com T > Af, como parte preliminar de um projeto que visa utilizar a liga como absorvedor dinâmico de vibração. Para obtenção das propriedades da liga foi utilizado ensaio de dureza, calorimetria diferencial de varredura (DSC), caracterização não-destrutiva dos módulos de elasticidade e amortecimento a partir das frequências naturais de vibração obtidas pela técnica de excitação por impulso, e ensaio de tração para levantar os platôs de transformação de fase e propriedades mecânicas do material. Primeiramente, barras cilíndricas (Ø 6 mm) e polidas de NiTi foram usinadas, após isso solubilizadas a 650ºC por 60 minutos com intuito de eliminar qualquer
transformação martensítica induzida por tensão e/ou temperatura e submetidas
posteriormente a tratamento térmico de 350ºC e 600ºC por 30 minutos, respectivamente. Foi observado que o tratamento a 350ºC apresentou formação de fase R a temperatura ambiente, a qual foi solubilizada a 600ºC. A presença de fase R levou à diminuição do módulo de elasticidade na liga. Após ensaios de tração foi observado que a condição 600ºC obteve a maior relação platô superior e inferior de
transformação de fase, podendo esta ser correlacionada com a área de histese,
possuindo assim a maior dissipação de energia, condição que teria provavelmente
um melhor comportamento como absorvedor dinâmico de vibração. ______________________________________________________________________________ ABSTRACT / With the emergence of new technologies, new materials are required for this evolution to happen, this is the case of alloys with shape memory. Alloys in particular Nickel Titanium (NiTi). A metal alloy that has unique properties such as damping, elasticity, recovery of the initial geometry being used in various fields like medical, dental, aerospace, automotive, construction and so on. In the electricity sector, specifically in transmission lines of electricity, which suffer from wind action and after some time fail due to fatigue at the fixing points to avoid such an event, are used dynamic vibration absorbers that reduce or eliminate the vibrations generated by action of wind energy absorbing. In this work the influence of the heat treatment was investigated in thermal and mechanical properties of an alloy NiTi pseudoelastic with T > Af, as a preliminary part of a project that aims to use the league as dynamic vibration absorber. To obtain the properties of the alloy was used hardness testing, differential scanning calorimetry (DSC), non destructive characterization of elastic and damping modules from the natural vibration frequencies obtained by the impulse
excitation technique and tensile test for raise the plateaus of phase transformation
and mechanical properties of the material . First, cylindrical bars (6 mm) and polished
NiTi were machined, after which solubilized at 650°C for 60 minutes in order to
eliminate any martensite induced by stress and/or temperature and subsequently
subjected to heat treatment of 350°C and 600°C for 30 minutes, respectively. It was
observed that the treatment at 350°C showed the formation of R phase at room temperature, which was solubilized at 600°C. The presence of R phase led to a decrease of the elastic modulus in the league. After tensile tests was observed that the condition 600°C had the highest respect upper and lower plateau phase
transformation, which may be correlated with the area of histese, thus having a greater energy dissipation, a condition that would likely have a better behavior as absorber dynamic vibration.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/15724 |
| Date | 20 August 2013 |
| Creators | Corrêa Filho, Luimar Nogueira |
| Contributors | Muterlle, Palloma Vieira |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds