PNIPAM (poly(N-Isopropylacrylamide)) is a well-known thermoresponsive polymer. Dissolved in water, it shows a structural change at 32 oC, above which the polymer folds together, and a phase separation occurs. The temperature where the polymer changes structure is known as the LCST (Lower Critical Solution Temperature), and can be modified by adding certain salts to the solution [1]. The mechanism by which the ionic components of the salts affect the LCST is not yet completely understood. The purpose of this master thesis is to study this mechanism. In order to investigate the mechanism, a combination of diffusion NMR and electrophoretic NMR was used, giving the effective charge per molecule which is directly proportional to the grade of association of ions to the polymer. The salts tested were: NaCl, NaClO4, NaSO4, NaI, NaSCN and CaCl2 from which the ClO4-, SCN-, and I- ions, as well as Cl- ions from CaCl2, were found to bind to PNIPAM.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-158534 |
Date | January 2013 |
Creators | Wiberg von Schantz, Cedrik |
Publisher | KTH, Skolan för kemivetenskap (CHE) |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds