Orientador: Paulo José Rocha de Albuquerque / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Civil, Arquitetura e Urbanismo / Made available in DSpace on 2018-08-23T09:53:31Z (GMT). No. of bitstreams: 1
LeonMogrovejo_DaphneRossana_M.pdf: 4385397 bytes, checksum: b52cd5308d53999c5da0e03e10716987 (MD5)
Previous issue date: 2013 / Resumo: Neste trabalho verificou-se a hipótese de que as fibras dispersas de papel Kraft, provenientes da reciclagem de sacos de cimento, podem ser utilizadas como estabilizante para melhorar as características e propriedades dos solos, por meio da análise do comportamento da mistura solo com fibras de polpa de celulose extraídas de sacos de cimento com três teores de fibra (5%, 10% e 15%) e dois tipos de solos (arenoso e argiloso). Não obstante, avaliou-se preliminarmente a influência desta adição nas características da água proveniente de uma possível percolação pelos solos, tendo em vista a possibilidade de contaminação do subsolo. Após realizar ensaios de laboratório (caracterização, compactação, permeabilidade e resistência) a partir de amostras deformadas, realizaram-se análises comparativas com as misturas. Constatou-se uma melhoria no desempenho das misturas quanto à resistência ao cisalhamento em ambos os solos, sendo observado melhor desempenho para o solo argiloso. Entretanto, verificou-se nas águas coletadas das misturas a partir de ensaios de permeabilidade, a tendência de aumento de condutividade elétrica, demanda química de oxigênio e dureza total quando comparados às águas dos dois solos sem fibra. Para verificar a validade dos resultados, realizaram-se análises estatísticas através do teste de Dunnett / Abstract: In this study was verified the hypothesis that the dispersed Kraft paper's fibers, resulted from the recycling process of cement bags, can be used as stabilizer in order to improve the characteristics and properties of soils, by analyzing of the behavior of mixture soil with cellulose pulp fibers extracted of cement bags with three fiber contents (5%, 10% and 15%) and two types of soils (sandy and clay). However, it was evaluated preliminarily the influence of this addition on the characteristics of water from a possible percolation through the soil, in view of the possibility of contamination of the subsoil After performing laboratorial experiments (physical characterization, compaction, permeability and resistance) from disturbed samples, were performed comparative analyses with the mixtures. It was noted an improvement in the performance of the mixtures when regarding shear resistance in both soils, and was observed even better performance in the clay soil. However, the collected samples of the mixtures from permeability tests presented a tendency of increased of electrical conductivity, chemical oxygen demand and total hardness when compared to the waters of the two soils without fiber. Statistical analyzes were performed to check the validity of the results using Dunnett test / Mestrado / Geotecnia / Mestra em Engenharia Civil
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/258567 |
| Date | 23 August 2018 |
| Creators | León Mogrovejo, Daphne Rossana, 1986- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Albuquerque, Paulo José Rocha de, 1964-, Carvalho, David de, Segantini, Antonio Anderson da Silva |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Programa de Pós-Graduação em Engenharia Civil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 193 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0035 seconds