This work reports on the synthesis, characterization and the physicochemical properties of novel unsymmetrically substituted zinc phthalocyanines: namely tris{11,19, 27-(1,2- diethylaminoethylthiol)-2-(captopril) phthalocyanine Zn ((ZnMCapPc (1.5)), hexakis{8,11,16,19,42,27-(octylthio)-1-(4-phenoxycarboxy) phthalocyanine} Zn (ZnMPCPc(1.7)) and Tris {11, 19, 27-(1,2-diethylaminoethylthiol)-1,2(caffeic acid) phthalocyanine} Zn ((ZnMCafPc (1.3)). Symmetrically substituted counterparts (tetrakis(diethylamino)zinc phthalocyaninato (3.8), octakis(octylthio)zinc phthalocyaninato (3.9) and tetrakis (carboxyphenoxy)zinc phthalocyaninato (3.10) complexes) were also synthesized for comparison of the photophysicochemical properties and to investigate the effect of the substituents on the low symmetry Pcs. The complexes were successfully characterized by IR, NMR, mass spectral and elemental analyses. All the complexes showed the ability to produce singlet oxygen, while the highest triplet quantum yields were obtained for 1.7, 1.5 and 3.9 (0.80, 0.65 and 0.62 respectively and the lowest were obtained for 1.3 and 3.10 (0.57 and 0.47 respectively). High triplet lifetimes (109-286 μs) were also obtained for all complexes, with 1.7 being the highest (286 μs) which also corresponds to its triplet and singlet quantum yields (0.80 and 0.77 respectively). The photosensitizing properties of low symmetry derivatives, ZnMCapPc and ZnMCafPc were investigated by conjugating glutathione (GSH) capped silver nanoparticles (AgNP). The formation of the amide bond was confirmed by IR and UV-Vis spectroscopies. The photophysicochemical behaviour of the novel phthalocyanine-GSH-AgNP conjugates and the simple mixture of the Ag NPs with low the symmetry phthalocyanines were investigated. It was observed that upon conjugation of the phthalocyanines to the GSH-AgNPs, a blue shift in the Q band was induced. The triplet lifetimes and quantum yields improved upon conjugation as compared to the phthalocyanines (Pc) alone. Complex 1.5 triplet lifetimes increased from 109 to 148 and triplet quantum yield from 0.65 to 0.86 upon conjugation. Fluorescence lifetimes and quantum yields decreased for the conjugates compared to the phthalocyanines alone, due to the quenching caused by the Ag NPs. The antimicrobial activity of the zinc phthalocyanines (complexes 1.3 and 1.5) and their conjugates against Escherichia coli was investigated. Only 1.3 and 1.5 complexes were investigated because of the availability of the sample. In general phthalocyanines showed increase in antibacterial activity with the increase in phthalocyanines concentration in the presence and absence of light. The Pc complexes and their Ag NP conjugates showed an increase in antibacterial activity, due to the synergistic effect afforded by Ag NP and Pcs. Improved antibacterial properties were obtained upon irradiation. 1.5-AgNPs had the highest antibacterial activity compared to 1.3-AgNPs conjugate; these results are in agreement with the photophysical behaviour. This work demonstrates improved photophysicochemical properties of low symm
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:rhodes/vital:4291 |
| Date | 10 June 2013 |
| Creators | Rapulenyane, Nomasonto |
| Publisher | Rhodes University, Faculty of Science, Chemistry |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Masters, MSc |
| Format | 134 p., pdf |
| Rights | Rapulenyane, Nomasonto |
Page generated in 0.0016 seconds