Orientador: Edison Bittencourt / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-27T14:50:33Z (GMT). No. of bitstreams: 1
Verceze_ArmandoValladas_M.pdf: 3062706 bytes, checksum: 0e14b20018f95cd0fb842992c96ca734 (MD5)
Previous issue date: 1996 / Resumo: Em Hemoterapia,tem-se utilizado bolsas múltiplas para a coleta e fracionamento de sangue e seus derivados. A característica especial destas bolsas é quanto à variação do tempo de estocagem para os concentrados de plaquetas, que depende de
propriedades como a permeabilidade ao oxigênio, considerado fator importante para o metabolismo das plaquetas. Tomando como padrão o filme de PVC plastificado com DOP (di-2-etilhexilftalato), de espessura padrão 370 micra, com gravação usual por
jateamento, foi estudado o filme denominado PL5, plastificado com o mesmo DOP, com espessura reduzida para 350 micra, com gravação especial, piramidal, regular e o filme de PVC plastificado com TOTM (tri-octil trimelitato) de espessura 370 micra, com gravação usual por jateamento. As modificações causadas pelo tipo de gravação foram avaliadas pelo estudo da permeabilidade ao oxigênio, com filmes da mesma espessura aparente, utilizando diferentes gravações e diferentes plastificantes (DOP e TOTM). Para caracterização da compatibilidade bio-toxicológica foram estudados todos os metais e as substâncias exigidas em portarias do
Ministério da Saúde e norma ISO específica...Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: In hemoteraphy, multiple blood bags have been used to collect and fractionate blood and its derivatives. The special feature of such bags is related to the storage-time length variation of the platelet concentrates, which depends upon properties such as permeability to oxygen, considered a factor of high importance for the metabolism oh platelets. Having a PVC film, plasticized with DOP, as thick as 370 micra, made rugged by usual jet as a pattern, a film named PL5, plasticized with the same DOP which
was thinned to 350 micra and was regularly, pyramid-like rugged, as well as a PVC film plasticized with TOTM, as thiek as 370 micra, made rugged by usual jet were studied. The changes caused by the kind of rugosity were evaluated by a study on the permeability to oxygen in films with the same thickness using different techniques to make them rugged and different plastieizers ( DOP and TOTM ).
ln order to characterize the bio-toxicological compatibility, all the metals and substances required by regulations of the Ministry of Health and specific ISO norm were studied...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266472 |
| Date | 15 February 1996 |
| Creators | Verceze, Armando Valladas |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Bittencourt, Edison, 1941-, Mei, Lucia Helena Inocentini, Arruda, Valder Roberval |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Unknown |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 89f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds