Orientador: Marcos Nogueira Eberlin / Dissertação (mestrado) - Universidade Estadual de Campinas. Instituto de Quimica / Made available in DSpace on 2018-07-27T08:59:46Z (GMT). No. of bitstreams: 1 Meurer_EduardoCesar_M.pdf: 3963120 bytes, checksum: c38b204edd931b6c04f463dd76f64197 (MD5) Previous issue date: 2000 / Mestrado

Orientador: Edison Bittencourt / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-27T14:50:33Z (GMT). No. of bitstreams: 1 Verceze_ArmandoValladas_M.pdf: 3062706 bytes, checksum: 0e14b20018f95cd0fb842992c96ca734 (MD5) Previous issue date: 1996 / Resumo: Em Hemoterapia,tem-se utilizado bolsas múltiplas para a coleta e fracionamento de sangue e seus derivados. A característica especial destas bolsas é quanto à variação do tempo de estocagem para os concentrados de plaquetas, que depende de propriedades como a permeabilidade ao oxigênio, considerado fator importante para o metabolismo das plaquetas. Tomando como padrão o filme de PVC plastificado com DOP (di-2-etilhexilftalato), de espessura padrão 370 micra, com gravação usual por jateamento, foi estudado o filme denominado PL5, plastificado com o mesmo DOP, com espessura reduzida para 350 micra, com gravação especial, piramidal, regular e o filme de PVC plastificado com TOTM (tri-octil trimelitato) de espessura 370 micra, com gravação usual por jateamento. As modificações causadas pelo tipo de gravação foram avaliadas pelo estudo da permeabilidade ao oxigênio, com filmes da mesma espessura aparente, utilizando diferentes gravações e diferentes plastificantes (DOP e TOTM). Para caracterização da compatibilidade bio-toxicológica foram estudados todos os metais e as substâncias exigidas em portarias do Ministério da Saúde e norma ISO específica...Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: In hemoteraphy, multiple blood bags have been used to collect and fractionate blood and its derivatives. The special feature of such bags is related to the storage-time length variation of the platelet concentrates, which depends upon properties such as permeability to oxygen, considered a factor of high importance for the metabolism oh platelets. Having a PVC film, plasticized with DOP, as thick as 370 micra, made rugged by usual jet as a pattern, a film named PL5, plasticized with the same DOP which was thinned to 350 micra and was regularly, pyramid-like rugged, as well as a PVC film plasticized with TOTM, as thiek as 370 micra, made rugged by usual jet were studied. The changes caused by the kind of rugosity were evaluated by a study on the permeability to oxygen in films with the same thickness using different techniques to make them rugged and different plastieizers ( DOP and TOTM ). ln order to characterize the bio-toxicological compatibility, all the metals and substances required by regulations of the Ministry of Health and specific ISO norm were studied...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química

Orientadores : Leila Peres, Jose Carlos Cunha Petrus / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-03T02:46:17Z (GMT). No. of bitstreams: 1 Bassetti_FatimadeJesus_D.pdf: 11629729 bytes, checksum: eb598e6620d1c60528abf54200242074 (MD5) Previous issue date: 2002 / Resumo: Primeiramente foi feita a preparação de membranas poliméricas microporosas assimétricas, através da técnica de inversão de fases. O poli (fluoreto de vinilideno)-PVDF foi utilizado puro, ou associado ao cloreto de lítio e a um dos seguintes aditivos poliméricos: poli(acetato de vinila)-PVAc ou polietilenoglicol - em diversas concentrações. A polietersulfona-PES também foi utilizada pura, ou associada a polivinilpirrolidona-PVP, de diversas massas moleculares médias: 10.000, 40.000 e 360.000 g/gmol, e em diversas concentrações. O solvente utilizado foi a N, N-dimetilformamida - DMF. A caracterização das soluções poliméricas e das membranas preparadas foi feita através das seguintes técnicas: Viscosimetria, Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Infravermelho com Transformada de Fourier (FTIR), Calorimetria Exploratória Diferencial (DSC), e ensaios de permeabilidade à água e retenção de albumina de soro bovino (BSA). O aumento das concentrações dos polímeros base (PVDF ou PES), levou à formação de membranas de maior espessura, pele filtrante com menor diâmetro médio e/ou número de poros, subcamada com menores cavidades e maior região esponjosa. De um modo geral, aumento das concentrações dos aditivos LiCl, PEG e PVAc na solução polimérica de PVDF levou à formação de membranas de maior espessura, maior porosidade superficial, e subcamada com maiores cavidades e menores regiões esponjosas. O aumento da massa molecular média da PVP levou à formação de membranas mais espessas, com menor porosidade superficial e, menor permeabilidade. A seguir, procedeu-se a seleção das melhores membranas preparadas, através da ultrafiltração de soro de queijo (pH 6,5) e de solução a 1,5% em massa, de poli (álcool vinílico) (PVA), sob as seguintes condições operacionais: temperatura de 50°C, pressão de 300 kPa e velocidades tangenciais de 0,64 m.s-1(soro) e 0,5 m.s-1 (PVA). As membranas de melhor desempenho apresentaram um fluxo permeado no estado estacionário, de cerca de 40 kg.h-1.m-2 para o soro de queijo e de 11 kg.h-1.m-2 para a solução de PV A, compatíveis ou até superiores aos relatados na literatura, para aplicações semelhantes. A membrana F3 (16%PVDF/3%LiCI), selecionada entre as melhores, foi utilizada no estudo da influência da variação dos parâmetros operacionais: temperatura, pressão e velocidade tangencial, na ultrafiltração de soro de queijo e de solução a 0,8 % em massa de PVA. A temperatura e a velocidade tangencial foram os parâmetros que influenciaram mais fortemente na taxa de permeação. Por último, aplicou-se um Modelo Matemático de Resistências em Série (membrana, colmatagem e camada de gel), na simulação do fluxo permeado, com a variação dos parâmetros operacionais, tanto do soro de queijo, quanto da solução de PVA e a comparação com as curvas experimentais obtidas. O modelo representou bem o efeito da variação dos parâmetros operacionais testados, no fluxo permeado para a solução de PVA. Para o soro de queijo, na maioria dos casos, o modelo também correspondeu muito bem ao fenômeno observado. A resistência da camada de gel, em comparação com as demais também calculadas, foi a grande responsável pelo declínio do fluxo permeado, tanto para o soro de queijo, quanto para a solução de PVA / Abstract: This work starts with the preparation of asymmetric microporous polymeric membranes through phase inversion technique by immersion-coagulation in the presence of a non-solvent. The poly (vinylidene fluoride)-PVDF was used pure or blended with lithium chloride and one of the following polymeric additives: poly (vinyl acetate)-PVAc or poly (ethylene glycol)-PEG, of various concentrations. The polyethersulfone -PES was also utilized pure or blended with polivinylpyrrolidone-PVP of different average molecular weights such as: 10,000 40,000 and 360,000 g/gmol, in various concentrations. The solvent utilized in every case N,N-dimethylformamide- DMF. The characterization of the polymeric solutions and the prepared membranes was carried out through the following techniques: Viscosimetry, Electron Microscopy, Fourier Transformed Infra-Red Spectroscopy, Differential Scanning Calorimetry, and water permeability tests and retention of bovine serum albumin. An increase in base polymer concentrations (PVDF or PES) led to the formation of thicker membranes, filtering skins with smaller mean diameters and/or number of voids, smaller cavity sub-Iayers, larger spongy regions and, therefore, a lower permeability. In general, the increase in the concentrations of additives LiCI, PEG and PV Ac concentrations, in the PVDF polymeric solution, led to thicker membranes formation, higher superficial porosity, larger cavity sub-Iayers and smaller spongy region. The PVP mean molecular weight increase resulted in thicker membrane formation with lower superficial porosity and permeability. Afterwards, a selection of the best membranes prepared through ultrafiltration of whey (pH 6.5) and PV A 1.5 % wt solution was done. The operational conditions were: temperature of 50 o C, pressure of 300 kPa and tangential velocities of 0.64 m.s-1 (whey) and 0.50 m.s-1 (PVA). The best performance membranes showed a steady state permeate flux of 40 kg.h-1.m-2 of whey and, 11 kg.h-1.m-2 of PVA solution. These figures are comparable with, and even higher than, those reported in the literature for similar applications. The F3 membrane (16%PVDF/3%LiCI), was selected as among the best ones to be used for the study of the influence of the operational parameters: temperature, pressure and tangential velocity, for the ultrafiltration of cheese whey and PV A 0.8 % wt solution. For both cheese whey and the PVA solution, the temperature and tangential velocity were the most influencing parameters on the permeating rate. At last, a serial resistances mathematical model (membrane, fouling and gel layer) was tested for permeate flux simulation. Both the whey and PVA solution operational parameters were varied. Also, the calculated and observed permeate flux curves were compared. For the PVA solution permeate flux, the model simulated adequately the variations in the operational parameters variation tested. As to whey, the results mostly showed good agreements. Among the different model resistances, the gel layer one had the strongest influence on the permeate flux decrease. This was valid for both cheese whey and PVA solution / Doutorado / Ciencia e Tecnologia de Materiais / Doutor em Engenharia Química

Orientador: Edison Bittencourt / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-01T10:14:18Z (GMT). No. of bitstreams: 1 Trochmann_JoseLuizLino_M.pdf: 3861994 bytes, checksum: 5b3f668441856f2e55953e941160192b (MD5) Previous issue date: 2000 / Resumo: Existem fortes demandas por novos materiais poliméricos para lentes oftálmicas, com melhores propriedades físicas e menores custos. As resinas de policarbonatos são de longe as mais utilizadas comercialmente, porém apresentam baixo índice de refração, resistência ao calor e ao impacto. Alternativas aos policarbonatos são necessárias. A compatibílização das especificações de resistência ao calor e de resistência ao impacto é um dos maiores desafios na obtenção destas resinas. Neste trabalho investigou-se o uso de modelos de predição de propriedades físicas, como ferramenta no desenvolvimento de resinas ópticas. Foram estudadas as copolimerizações altemada e em bloco do estireno com di - metacrilatos do etileno glicol. Fazendo uso de modelos e com as especificações de: massa específica P I índice de refração n20o, temperatura de transição vítrea Tg, módulo de cisalhamento G, resistência ao calor e ao impacto foram selecionados os agentes de reticulação, que atendiam a todas especificações ao mesmo tempo. Foram estimadas as frações de alimentação dos agentes de reticulação da mistura reacional. O processo de cura escolhido foi o fotoquímico, por ser mais rápido e de menor custo que os processos de cura termoquímica convencionais. Diversos tipos e concentrações de fotoiniciadores foram testados. Os índices de refração foram medidos em refratômetro de Abbe e comparados com os valores previstos pelo modelo de Lorentz Lorenz. As temperaturas de transição vítrea foram medidas por análise termo e foto calorimétrica, DPC / Abstract: There is a large demand form new polymeric material for use in ophthalmic lens with improved physical properties and lower costs. The polycarbonates resins are by far the most used in the industry. To meet the heat and strength resistance specífications at the same time is one of the most challenges in the development of those resins. There is a large demand form new polymeric material for use in ophthalmic lens with improved physical properties and lower costs. The polycarbonates resins are by far the most used in the industry. To meet the heat and strength resistance specífications at the same time is one of the most challenges in the development of those resins. The photochemical process was elected due to the simplicity and general lower costs compared with the conventional thermochemical processo Several different photoinitiators and concentrations were tested. The refractive index of comonomers separately, cured and uncured resins were measured in an Abbe's refratometer and compared with the data trom the Lorentz - Lorenz prediction model. The glass transition temperature of cured resins were measured using the thermo - calorimetric techniques analyses, DSC-DPC, and compared with data from the van Krevelen's prediction model, for addictive contribution groups. The shear moduli of cured resins were measured with DMA and compared with data trom Treloar - Smith's prediction model, for the respective crosslinking density and length. The formulations selected by using the models, were casting and UV - irradiated with several different UV-light and dark period ratios at constant temperature. Samples were take at predefined curing times for analysis of: conversion, Shore "D" hardness, refractive index, glass transition temperature, shear modulus, softening temperature, strength resistance, heat resistance and visual inspection for defects. The deviation between lhe predicted density data and measured values was about + 1.5%. lhat can be considered a good approximation; for the refractive indexdeviation was about +0,4% Ihat is an excellent approximation; . the glass transition temperature deviations were around +5%. Ihat is also excellent approximation considering the nature of Ihis physical property and finally for lhe shear modulus deviation were between + 1 O a 20% for the less rich in di- melhaaylates, 0.33 til! 0.5. Above those values the model showed a much larger deviation due to lhe entropy elasticity associated to the thennal movements of the bridged segments of the crosslinking agents in the network / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química