The effect of a controlled oxygen admixture to a plasma nitrocarburizing process using active screen technology and an active screen made of carbon was investigated to control the carburizing potential within the plasma-assisted process. Laser absorption spectroscopy was used to determine the resulting process gas composition at different levels of oxygen admixture using O2 and CO2, respectively, as well as the long-term trends of the concentration of major reaction products over the duration of a material treatment of ARMCO® iron. The short-term studies of the resulting process gas composition, as a function of oxygen addition to the process feed gases N2 and H2, showed that a stepwise increase in oxygen addition led to the formation of oxygen-containing species, such as CO, CO2, and H2O, and to a significant decrease in the concentrations of hydrocarbons and HCN. Despite increased oxygen concentration within the process gas, no oxygen enrichment was observed in the compound layer of ARMCO® iron; however, the diffusion depth of nitrogen and carbon increased significantly. Increasing the local nitrogen concentration changed the stoichiometry of the ε-Fe3(N,C)1+x phase in the compound layer and opens up additional degrees of freedom for improved process control.
Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:92600 |
Date | 12 July 2024 |
Creators | Böcker, Jan, Dalke, Anke, Puth, Alexander, Schimpf, Christian, Röpcke, Jürgen, van Helden, Jean-Pierre H., Biermann, Horst |
Contributors | Technische Universität Bergakademie Freiberg |
Publisher | MDPI |
Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
Language | English |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, doc-type:article, info:eu-repo/semantics/article, doc-type:Text |
Rights | info:eu-repo/semantics/openAccess |
Relation | 2076-3417, https://doi.org/10.3390/app11219918 |
Page generated in 0.0019 seconds