Previous issue date: 2015-02-20 / Conselho Nacional de Desenvolvimento Científico e Tecnológico - CNPq / A capacidade produtiva de poços de petróleo está diretamente relacionada à
qualidade da cimentação. A cimentação tem como objetivo isolar as zonas
indesejáveis, da zona produtora. Em alguns casos, cada vez mais frequente e usual,
para atingir a zona desejada durante a perfuração, são necessários desvios de alto
ângulo e com grandes extensões horizontais, submetendo o poço à elevada
variação de gradiente geotérmico. A operação de cimentação de poços direcionais e
horizontais requer condições de pastas de cimento específicas, com maior fluidez e
estabilidade e tempos de pega específicos. Outra grande preocupação é o
comportamento mecânico da região cimentada em poços submetidos à estimulação
da produção de óleo por métodos térmicos de recuperação. Onde, devido à
dilatação térmica do revestimento metálico, não acompanhada na mesma proporção
pela bainha de cimento, ocorre formação de trincas no material cimentante,
comprometendo a integridade mecânica do anular. Compósitos cimentantes
contendo polímeros vem sendo estudados para garantir melhor qualidade de
cimentação de poços sujeitos a condições de alta temperatura, garantindo maior
coeficiente de dilatação térmica ao cimento e maior adesão ao revestimento. Nesse
contexto foram desenvolvidos compósitos cimentantes contendo polímeros para
operações de cimentação de poços direcionais com grandes extensões horizontais,
sujeitos à condição de injeção de vapor. Foram estudadas as influências da adição
poliuretana e quitosana nas pastas de cimento no estado fresco e no estado
endurecido, por meio de testes laboratoriais normatizados. As pastas contendo
poliuretana e quitosana apresentaram boa fluidez, estabilidade de densidade e
auxiliam no controle de filtrado. / The productive capacity of oil wells is directly related to the quality of cementing.
Cementing has the objective to isolate the undesirable areas of the producing zone.
In some cases, increasingly frequent and usual, to achieve the desired zone during
drilling, are required angle deviations and large horizontal extension, subjecting the
well to the high variation in geothermal gradient. The cementing operation of
directional and horizontal wells requires specific conditions of cement slurries with
greater fluidity and stability, and grip specific times. Another major concern is the
mechanical behavior of cemented wells region undergoing stimulation of oil recovery
by thermal methods. Where, because of thermal expansion of the metal coating, not
accompanied by the same ratio of cement sheath, crack formation occurs in the
cementitious material, compromising the mechanical integrity of the void. Cements
composite containing polymers has been studied to ensure a better quality of
cementing wells subject to high temperature conditions, ensuring greater coefficient
of thermal expansion of the cement and greater adherence to coating. In this context
were developed cements composite containing polymers for cementing operations
directional wells with large horizontal runs, subject to steam injection condition. The
influences of polyurethane addition and chitosan were studied in cement slurries in
fresh and hardened state, through standardized laboratory tests. Slurries containing
polyurethane and chitosan had good fluidity, density stability and assist in the filtrate
control.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/25659 |
| Date | 20 February 2015 |
| Creators | Costa, Filipe Johnatan Martins Dantas |
| Contributors | 15724520800, Freitas, Júlio Cézar de Oliveira, 00957245408, Fernandes, Maria Roseane de Pontes, 03869604450, Martinelli, Antonio Eduardo |
| Publisher | PROGRAMA DE PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds