Orientador: Cecilia Amelia de Carvalho Zavaglia / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Eletrica e de Computação / Made available in DSpace on 2018-07-22T00:42:36Z (GMT). No. of bitstreams: 1
Malmonge_SoniaMaria_D.pdf: 27621772 bytes, checksum: 36c16f80f546209e3427eae886b814e0 (MD5)
Previous issue date: 1997 / Resumo: Foi realizado um estudo com hidrogéis sintéticos, para a obtenção de biomaterial com caracteristicas adequadas ao uso no reparo de defeitos da cartilagem articular. Amostras de hidrogéis de poli(2-hidróxi etil metacrilato) (poliHEMA), blendas do tipo redes semi interpenetrantes - sIPN de poliHEMA com acetato de celulose (poliHEMA-AC) e de poliHEMA com poli(metacrilato de metila-co-ácido acrílico) (poliHEMA-poli(MMA-co-AA) foram obtidas por polimerização térmica e caracterizadas quanto à capacidade de absorção de água e de solução salina; quanto ao comportamento mecânico, através de ensaios de fluência a indentação e quanto à citotoxicidade frente a cultura de células in vitro. Os resultados mostraram que é possível melhorar o comportamento mecânico de hidrogéis de poliHEMA, através da variação na quantidade de agente de reticulação ou da obtenção de blendas de poliHEMA com polímeros lineares, porém o aumento das propriedades mecânicas é sempre acompanhado de uma diminuição da capacidade de absorção de água. Nenhum dos hidrogéis estudados apresentou efeito citotóxico frente a cultura de células VERO. A blenda poliHEMA-poli(MMA-co-AA) possibilitou uma melhora das propriedades mecânicas do hidrogel de poliHEMA, sem diminuirmuito a sua capacidade de absorção de água e permitiu a incorporação de grupos negativos fixos a estrutura macromolecular, mimetizando assim a matriz extracelular da cartilagem articular e apresentando características semelhantes as da cartilagem hialina... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: This work shows a study carried out with synthetic hydrogels aiming the obtention of a biomaterial to be used in the repair of articular cartilage defects. Hydrogels samples of poly (2-hydroxy ethyl methacrylate) (polyHEMA) and blends of polyHEMA with cellulose acetate (CA) or poly(methyl methacrylate-co-acrylic acid) (poly(MMA-co-AA)) was obtained by thermal polymerization and the following characterisation procedures was carried out: determination of the equilibrium water content and saline solution content, evaluation of the mechanical behaviour by creep indentation tests and cytotoxicity through in vitro tests. The results showed that it is possible to improve the mechanical behaviour of the polyHEMA hydrogels by-changing the crosslinking agent amount or by blending polyHEMA with linear polymers. The mechanical properties improve was accompanied by a decrease in the equilibrium water content and let to the incorporation of negative fixed charges to the macromolecular network, mimicking the extracelular matrix of the hyaline cartilage. This hydrogel showed characteristics similar to that one of hyaline cartilage and was used in a in vivo test that showed its potential for using in the repair of articular cartilage defects. The hydrogel implant did not show significative inflammatory reaction, let to a decrease in the synovial inflammations and improved the repair of the articular cartilage defects performed in the intercondilian region of rat femur, by forming an articular surface showing better biomechanical characteristics than the surface of biological repair in case of control defects... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Doutorado / Automação / Doutor em Engenharia Elétrica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/260668 |
| Date | 22 July 2018 |
| Creators | Malmonge, Sonia Maria |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Zavaglia, Cecília Amélia de Carvalho, 1954- |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Elétrica e de Computação, Programa de Pós-Graduação em Engenharia Elétrica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 133f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds