The aim of this research work was to improve the compatibility of polymer blends made from poly(lactic acid) and natural rubber (PLA/NR blends) by using modified natural rubber as a compatibilizer. Natural rubber was chemically modified into two categories: natural rubber grafted poly(vinyl acetate) copolymer (NR-g-PVAc) and block copolymers (PLA-NR diblock copolymer and PLA-NR-PLA triblock copolymer). PLA/NR blends were prepared by melting blending in a twin screw extruder and compression molded to obtain a 2-mm thick sheet. The blends contained 10-20 wt% of NR and modified NR, and the impact strength and tensile properties were investigated. The compatibilization effect was determined by DMTA, DSC and SEM. NR-g-PVAc was synthesized by emulsion polymerization to obtain different PVAc graft contents (1%, 5% and 12%). Characterization by DMTA showed an enhancement in miscibility of the PLA/NR-g-PVAc blends. NR-g-PVAc could be used as a toughening agent of PLA and as a compatibilizer of the PLA/NR blend. The block copolymers were synthesized following two routes: (1) hydroxyl telechelic natural rubber (HTNR) and lactide and (2) HTNR and PLA prepolymer. In the former route, lactide was in situ polymerized via a ring opening polymerization to be a PLA block segment during block copolymerization. In the latter route PLA prepolymer was synthesized by a condensation polymerization of L-lactic acid prior to block copolymerization. Both block copolymers acted as good compatibilizers for the PLA/NR blend by increasing the impact strength and decreasing the NR particle size. Triblock copolymers provided higher impact strength than diblock copolymers, and they were a less effective compatibilizer than NR-g-PVAc. In contrast to NR and NR-g-PVAc, the block copolymer was not a good toughening agent for PLA.
| Identifer | oai:union.ndltd.org:CCSD/oai:tel.archives-ouvertes.fr:tel-01018026 |
| Date | 11 December 2013 |
| Creators | Chumeka, Wannapa |
| Publisher | Université du Maine |
| Source Sets | CCSD theses-EN-ligne, France |
| Language | English |
| Detected Language | English |
| Type | PhD thesis |
Page generated in 0.0021 seconds