Orientadores: Lucia Helena Innocentini Mei, Joceli Maria Giacomini Angelini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-08-15T13:39:32Z (GMT). No. of bitstreams: 1
Noronha_Fabio_M.pdf: 6615415 bytes, checksum: f72688fb0000126501c64a7267950cb0 (MD5)
Previous issue date: 2010 / Resumo: Atualmente, os materiais utilizados como isoladores elétricos vêm sendo substituídos por materiais poliméricos por apresentarem vantagens em relação aos isoladores cerâmicos. Dentre estas vantagens, podem-se citar maior desempenho, melhor resistência ao vandalismo e menor peso. O objetivo desta dissertação foi o estabelecimento de desenvolver requisitos de desempenho para os Isoladores Poliméricos (EPDM- Monômero Dieno/Etileno/Propileno e Silicone) usados na rede elétrica, através de resultados obtidos em ensaios de envelhecimento natural e artificial, tendo como enfoque as linhas de transmissão de 69 kV e 138 kV. Foi realizado um estudo do estado da arte em Isoladores Poliméricos e do estado atual de aplicação e desempenho dos mesmos em campo. Estudos experimentais foram desenvolvidos em produtos retirados de campo e produtos novos, envelhecidos artificialmente em laboratório, segundo metodologias aplicáveis a polímeros. Em paralelo foram estudadas mantas elastoméricas de Silicone e EPDM para elaboração de critérios comparativos. Através dos resultados obtidos, foram sugeridos alguns requisitos de desempenho que poderão ser utilizados em especificações dos mesmos. Nesta dissertação, são apresentados, principalmente, estes resultados obtidos por meio das técnicas de ensaio de Tensões Elétricas, Rugosidade, Densidade, Dureza, FTIR-Infravermelho com Transformada de Fourier, DSC-Calorimetria Exploratória, DMTA-Análise Térmica Dinâmico Mecânica e Resistência à Tração. Os resultados obtidos mostraram a importância de controle da rugosidade bem como da necessidade de aditivação do polímero com sistema de termo e foto estabilização / Abstract: Currently, the materials used as electrical insulators are being replaced by polymeric materials have advantages as compared to ceramic insulators. Among these advantages, we can cite higher performance, better resistance to vandalism and lower weight. The objective of this thesis was the establishment of developing performance requirements for Polymeric Insulators (EPDM monomer diene / ethylene / propylene and Silicone) used in power systems, through results from trials of natural and artificial aging, focusing on the lines transmission of 69 kV and 138 kV. We conducted a study of the state of the art in Polymeric Insulators and current state of implementation and performance of the same field. Experimental studies have been developed into products removed from the field and new, artificially aged in the laboratory, according to the methods applied to polymers. Were studied in parallel webs of silicone elastomer and EPDM for developing benchmarks. Through the results, suggested some performance requirements that could be used in the same specifications. In this thesis, are presented, mainly, these results obtained by the techniques of test voltages, roughness, density, hardness, FTIR-Fourier Transform Infrared, Scanning Calorimetry-DSC, DMTA Dynamic-Mechanical Thermal Analysis and Tensile Strength . The results showed the importance of controlling the roughness and the need for additives with the polymer system and picture stabilization term / Mestrado / Ciencia e Tecnologia de Materiais / Mestre em Engenharia Química
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267098 |
Date | 15 August 2018 |
Creators | Noronha, Fabio |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Angelini, Joceli Maria Giacomini, Mei, Lúcia Helena Innocentini, 1953-, Peres, Leila, Aragão, Bernardo Jose Guilherme de |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 79 f. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds