In this study SBA-15 mesoporous silica template was synthesized and used as a sacrificial template in the preparation of ordered mesoporous carbon material. A chemical vapour deposition (CVD) technique using LPG or alternatively sucrose, pyrolyzed upon a mesoporous Si matrix were used to produce nanostructured ordered mesoporous carbon (OMC) with graphitic character after removing the Si template. The sucrose method was found to be a suitable route for preparing OMC. The OMC was used as a conductive three dimensional porous support for depositing catalytic nanophase Pt metal. Deposition of Pt nanoparticles on OMC was accomplished using a CVD method with Pt(acac)2 as a precursor. The synthesized nano-composite materials were characterized by several techniques such as, HRTEM, HRSEM, EDS, XRD, BET, TGA, FT-IR and CV.
Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:uwc/oai:UWC_ETD:http%3A%2F%2Fetd.uwc.ac.za%2Findex.php%3Fmodule%3Detd%26action%3Dviewtitle%26id%3Dgen8Srv25Nme4_8474_1320738516 |
Date | January 2011 |
Creators | Saban, Waheed |
Source Sets | South African National ETD Portal |
Language | English |
Detected Language | English |
Type | Thesis and dissertation |
Format | |
Coverage | ZA |
Rights | Copyright: University of the Western Cape |
Page generated in 0.0049 seconds