Orientador: Luis Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-07T21:42:27Z (GMT). No. of bitstreams: 1
PedrosaFilho_CelsodeFreitas_D.pdf: 1514708 bytes, checksum: 68479f75bac6f0d3bdbb5ec943719f31 (MD5)
Previous issue date: 2006 / Resumo: Neste estudo avaliou-se a resistência ao cisalhamento por extrusão de pinos de fibra de vidro, reembasados ou não com compósito, cimentados com cimento resinoso em dentina intra-radicular, avaliando os segmentos cervical, médio e apical. Selecionaram-se 20 incisivos bovinos com dimensões semelhantes, removendo a porção coronária, padronizando o comprimento das raízes em 16 mm. Após, incluiu-se as raízes em resina acrílica, realizando tratamento endodôntico e, então o preparo dos espaços para os pinos, dividindoas, em seguida, aleatoriamente em dois grupos com dez amostras cada. Os elementos do grupo 1 receberam pinos de fibra de vidro somente cimentados, e do grupo 2 pinos de fibra de vidro reembasados com compósito e posteriormente cimentados. Ao término dos procedimentos de cimentação, realizou-se a secção dos segmentos radiculares, submetendo, então, os corpos-de-prova ao teste push-out em máquina de ensaios universal, através de ponta ativa cilíndrica com 1 mm de diâmetro, à velocidade de 0,5 mm/min, até extrusão do retentor. Obteve-se os seguintes valores médios de resistência de união, em MPa: grupo 1, terços cervical = 6,24 ± 2,68(b), médio = 4,27 ± 2,00(b) e apical = 4,46 ± 2,82(b); grupo 2, terços cervical = 11,83 ± 1,69(a), médio = 11,81 ± 3,86(a) e apical = 10,39 ± 2,44(a). Submeteram-se os valores à análise de variância e ao teste de Tukey com nível de significância de 5%, indicadas acima através de letras diferentes. Os pinos de fibra de vidro reembasados com compósito apresentaram valores estatisticamente superiores de união em todos os segmentos radiculares quando comparados com pinos somente cimentados. Observou-se também a ausência de diferença significativa entre os terços radiculares avaliados para cada grupo distintamente. Os resultados demonstraram que a técnica de reembasamento mostrou-se efetiva em melhorar a retenção do pino de fibra de vidro estudado / Abstract: This study evaluated the bond strength of fiber posts, relined or not with composite resin, luted with resinous cement to radicular dentin, evaluating cervical, median and apical root segments. Twenty bovine incisors, with similar dimensions, were selected and cut 16 mm from the apical limit. The roots were embedded in acrylic resin and the radicular canals were root treated and post space prepared with a depth of 9 mm. Samples were randomly assigned to two groups of ten roots each. Group 1 received glass fiber posts (Fibrekor) luted with dual-cure resin cement (RelyX ARC) in association with a bonding system (Adper Single Bond). In Group 2 the same type of posts were relined with composite (P-60) for further cementation with the same materials used in Group 1. After cementation procedures roots were sectioned transversally and three sections, from cervical, medium and apical thirds were obtained. Push-out test was performed in a universal testing machine with a 1 mm diameter steel rod at cross-head speed of 0,5 mm/min until post extrusion. Collected data was statistically analyzed by twoway ANOVA and Tukey HSD test (p<0,05). The measured retention strengths for cervical, medium and apical thirds were: Group 1, 6.24 ± 2.68(b), 4.27 ± 2.00(b) and 4.46 ± 2.82(b) ; Group 2, 11.83 ± 1.69(a), 11.81 ± 3.86(a) and 10.39 ± 2.44(a). Glass fiber composite relined posts presented statistically higher retention values in cervical, medium and apical thirds when compared to non-relined posts. Within each group, no differences were found among radicular thirds. The results indicate that the tested technique showed effective improvement of glass fiber post retention strength / Doutorado / Dentística / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289716 |
| Date | 24 November 2006 |
| Creators | Pedrosa Filho, Celso de Freitas |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Martins, Luís Roberto Marcondes, 1960-, Junior, Jacy Ribeiro de Carvalho, Lopes, Lawrence Gonzaga, Nóbilo, Mauro Antonio de Arruda, Aguiar, Flávio Henrique Baggio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 122p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds