Orientadores : Saide Sarckis Domitti, Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T05:33:00Z (GMT). No. of bitstreams: 1
Almeida_MariaHelenaWaackde_D.pdf: 5508767 bytes, checksum: b03c3c13c9774dfa80be1f7537d1c28d (MD5)
Previous issue date: 2001 / Resumo: O objetivo desta pesquisa foi verificar os efeitos da combinação de gessos de inclusão na adaptação das bases de prótese total superior, confeccionadas com resina acrílica ativada termicamente, polimerizadas de acordo com os seguintes ciclos: convencional, calor seco e energia de microondas. Foram confeccionados quarenta e cinco modelos padrões em gesso pedra, a partir de um molde de borracha representando uma arcada superior desdentada. Sobre os modelos foram confeccionadas quarenta e cinco bases de prova, divididas aleatoriamente em três grupos de quinze elementos cada, baseados no tipo do gesso utilizado durante a fase de inclusão dos modelos. No Grupo l, as bases de prova foram incluídas em mufla pela técnica convencional, utilizando-se gesso comum e pedra. No Grupo lI, utilizando-se gesso comum e especial, e no Grupo III, gesso pedra e especial. Cada Grupo foi subdividido em três subgrupos, de acordo com o ciclo de polimerização ao qual as amostras foram submetidas: Subgrupo 1: polimerização através do ciclo convencional (74+2°C por 9 horas); Subgrupo 2: polimerização por calor seco (74+2°C por 9 horas); e Subgrupo 3: polimerização através de energia de microondas (900 W por 3 minutos). A seguir, as bases em resina foram fixadas em seus respectivos modelos com adesivo instantâneo. O conjunto base de prótese-modelo de gesso foi posicionado, fixado e seccionado em aparelho específico onde foram executados três cortes látero-Iaterais: A (anterior), B (médio) e C (posterior). A alteração dimensional ocorrida na resina acrílica foi avaliada por meio de um microscópio comparador, em cinco pontos referenciais. Os resultados numéricos foram submetidos à análise de 1 variância e ao teste de Tukey (5%). Concluiu-se que, independente dos demais fatores, o ciclo convencional mostrou o maior desajuste das bases de prótese em relação aos modelos. Quando o tipo de inclusão foi analisado em relação ao fator ciclo de polimerização, verificamos que as inclusões Comum/Especial e Pedra/Especial não apresentaram valores com diferença estatística significativa. Na inclusão Comum/Pedra o ciclo convencional apresentou o maior desajuste. Quando o fator corte foi analisado em função do ciclo de polimerização, notamos que no corte A, o ciclo convencional apresentou o maior desajuste. Quando os cortes foram analisados independente de outros fatores, houve diferença estatística significativa entre eles. O maior desajuste ocorreu no corte C. Quando os cortes foram analisados em relação ao tipo de inclusão independente de outros fatores, verificamos que nas inclusões Comum/Especial e Pedra/Especial, o maior desajuste ocorreu no corte C. Quando o tipo de inclusão foi observado independente de outros fatores, verificamos que a inclusão Comum/Pedra apresentou o menor desajuste / Abstract: he purpose of this study was to verify the effects of the combination of inclusion plaster in the adaptation of upper denture bases, made with heat-cured acrylic resin, ocurred under the influence of three cycles of polymerization: conventional, by dry heat and with microwave energy. Forty-five master casts were made in stone plaster from a rubber cast representing upper nondental arch. The forty-five experimental bases were made on the casts which were divided at randon into three groups of fifteen elements, based on the kind of plaster used during the inclusion phase of the casts. The casts with the experimental bases from Group I were included in flask by conventional technique, using commum plaster and stone. In the Group II, using commum plaster and special, and the Group II stone plaster and special. Each group was subdivided into three subgroups, according the polymerization cycle to which the casts were submitted: Subgroup 1: polymerization through the conventional cycle (74 + 2°e for nine hours). Subgroup 2: polymerization by dry heat (74 + 2° e for nine hours) and Subgroup 3: polymerization in Microwave Oven (900 W for 3 minutes). Next, the bases in resin were fixed on their casts with instantaneous adhesive. The plaster model - prosthesis bases set was positined, fixed and cut on an especific instrument, three lateral plane cuts were made: A (anterior), B (median) and e (posterior). The occurred dimensional alteration on the acrylic resin was evaluated with a comparator microscope in five referential points. The numerical results were submitted to a variance analysis and the Tukey Test (5%). It was concluded that, independent of other factors, the conventional cycle showed the biggest disadjustment of the denture bases in relation to the casts. When the kind of inclusion was analysed in relation to the cycle fa cto r of polymerization, it was verified that the Commum/Special and Stone/Special inclusions did not show statistic significative difference. In the Commum/Stone inclusion the conventional cycle showed the biggest disadjustment. When the cut factor was analysed in relation to the polymerization cycle, it was verified that in the A cut, the conventional cycle showed the biggest disadjustment. When the cuts were analysed independent of other factors, there was significative statistic difference among them. The biggest disadjustment occurred in the C cut. When the cuts were analysed in relation to the kind of inclusion independent of other factors, it was verified that in the Commum/Special and Stone/Special inclusions, the biggest disadjustment occurred in the C cut. When the kind of inclusion was analysed independent of other factors, it was verified that the Commum/Stone inclusion showed the smallest disadjustment / Doutorado / Protese / Doutor em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289955 |
| Date | 02 December 2001 |
| Creators | Almeida, Maria Helena Waack de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939-, Domitti, Saide Sarckis, 1932-2016, Filho, João Neudemir Arioli, Kimpara, Estevão Tomomitsu, Mesquita, Marcelo Ferraz |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 137p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds