Conselho Nacional de Desenvolvimento CientÃfico e TecnolÃgico / Materiais do tipo tungstÃnio bronze tÃm atraÃdo a atenÃÃo da comunidade cientÃfica por suas interessantes propriedades fÃsicas. Os tungstÃnios bronze hexagonais do tipo AxWO3 (onde A = K, Rb, Cs) por exemplo, sÃo supercondutores bem conhecidos. O RbBi1/3W8/3O9, particularmente, pertence a classe dos bronzes hexagonais de valÃncia balanceada com formula geral ABxW3-xO9 (A = Cs, K, Rb, Cs, Tl; B = Bi, Nb, Ta, Zr, Sc, etc.). Estes materiais dielÃtricos tÃm atraÃdo um grande interesse, uma vez que, eles exibem sucessivas transiÃÃes de fase, propriedades ferroelÃtricas e geraÃÃo de segundos harmÃnicos. O objetivo deste trabalho foi investigar as propriedades vibracionais do sistema dopado RbBi0,313Nd0,02W8/3O9 com um foco especial na dependÃncia dos modos vibracionais com a pressÃo e à baixas temperaturas. Embora a estrutura do cristal RbBi1/3W8/3O9 nÃo seja conhecida ainda, estudos de difraÃÃo de raios-x mostraram que os hexatungstatos de potÃssio e rubÃdio sÃo isoestruturais e a simetria mais provÃvel à a estrutura de camada ortorrÃmbica, Pbn21, Pbc21, Cmm2. Relatamos neste trabalho resultados de medidas a altas pressÃes hidrostÃticas no intervalo de 0,0-6,6 GPa, medidas de anÃlise tÃrmica diferencial e termogravimÃtricas (DTA-TG), medidas de espectroscopia Raman a baixas temperaturas no intervalo de 295-38 K, medidas de infravermelho à temperatura e pressÃo ambiente e de fotoluminescÃncia tambÃm à temperatura e pressÃo ambiente e cÃlculos clÃssicos de modos de vibraÃÃo. O RbBi1/3W8/3O9 foi dopado com um pequeno percentual do metal de transiÃÃo Nd com o objetivo de usÃ-lo, como Ãon sonda para realizaÃÃo de medidas de fotoluminescÃncia. Com este procedimento, observamos que o Nd, ocupa um sÃtio de baixa simetria. As medidas com pressÃo revelam que o RbBi0,313Nd0,02W8/3O9 apresenta uma transiÃÃo de fase estrutural reversÃvel em torno de 4 GPa quando submetido a altas pressÃes. Esta transiÃÃo està relacionada provavelmente a reorientaÃÃo das unidades octaÃdricas em torno do eixo c com sensÃveis mudanÃas no pseudo plano hexagonal ab. O material tambÃm apresenta provavelmente duas sutis transiÃÃes de fase a baixas temperaturas, uma em torno de 200 K e a outra em torno de 100 K. Estas transiÃÃes sÃo provavelmente devido a rotaÃÃes das unidades octaÃdricas em torno do eixo principal do cristal, sem, contudo modificar significativamente as distÃncias das ligaÃÃes W-O. As medidas de infravermelho revelam a existÃncia de molÃculas de Ãgua no material. As medidas de DTA-TG revelam que a Ãgua observada na amostra à superficial e tambÃm mostram que o material à estÃvel no intervalo de temperatura entre 30 oC e 600 oC. Pelo fato da estrutura deste material ainda nÃo ser conhecida na literatura. CÃlculos clÃssicos de dinÃmica de rede foram realizados no K0,26WO3, que possui assinatura Raman muito similar à do RbBi0,313Nd0,02W8/3O9. O objetivo deste trabalho foi entender os principais aspectos das propriedades vibracionais do K0,26WO3. De posse destes resultados, e devido a relaÃÃo prÃxima entre as estruturas, foi possÃvel discutir as modificaÃÃes estruturais observadas nos espectros Raman do material RbBi0,313Nd0,02W8/3O9 durante os experimentos com variaÃÃo de pressÃo e temperatura. Um aspecto importante dos resultados dos cÃlculos vibracionais foi a previsÃo de modos vibracionais tipos tubulares relacionados Ãs cavidades hexagonais do K0,26WO3. / Tungsten bronzes has attracted great attention owing to it is interesting physical properties. Hexagonal tungsten of the form AxWO3 (with A = K, Rb, Cs), are well know superconductors. The RbBi1/3W8/3O9 (RBW) material, belongs to the valence balanced hexagonal tungsten materials with ABxW3-xO9 stoichiometry (with A = Cs, K, Rb, Tl, and B = Bi, Nd, Ta, Zr, Sc, etc.) These materials present interesting physical properties like rich sequence of phase transitions (rich polymorphism), ferroelectric properties and second harmonic generation. Despite of the unknown structure of this system (we mean spatial symmetry), X-ray experiments suggest that Rubidium and cesium hexatungstates are isostructural with orthorhombic structure belonging possibly to Pbn21, Pbc21 or Cmm2 space group symmetry. The aim of this work was to investigate the vibrational properties of RbBi0,313Nd0,02W8/3O9 system, with special focus on the vibrational properties of this system under extreme conditions of pressure and temperature. We report in this work, a detailed study of Nd3+ doped RBW in witch we have performed light scattering high pressure experiment in the 0,0-6,6 GPa pressure range; light scattering low temperature experiment in the 300-38 K temperature range; DTA-TG experiments; photoluminescence experiments; and lattice dynamics phonons calculation in parent structure. Our results reveal that the RBW materials experiment a pressure induced structural phase transition (SPT) at around 4 GPa. This SPT is related to rotations of octahedral units around the c axis along with subtle changes in the ab pseudo hexagonal plane. Additionally we have observed two temperature induced SPT at around 200 K and 100 K. Both 4 GPa pressure induced and 200 K temperature induced SPT seems to be driven by similar mechanisms. The 100 K temperature induced SPT seems to involve more complex rotations of octahedral. Infrared and termogravimetric (TG-DTA) measurements reveal the observation of superficial water molecules in the RBW material. Termogravimetric measurements indicate that the RBW is stable up to 600 oC. We have performed Lattice dynamics phonon calculations on K0,26WO3 (RBW closely related structure with similar Raman features) in order to get insights on the vibrational properties of hexagonal tungstates. These results allowed us to interpret the transformation mechanisms of the observed pressure and temperature induced phase transitions. The lattice dynamics calculations revealed the existence of radial and tangential motions of oxygen atoms belonging to the hexagonal cavities. The tubular like modes command the dynamics of phase transitions in hexagonal tungsten systems.
Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:2312 |
Date | 16 February 2009 |
Creators | Janilson dos Santos Coelho |
Contributors | Waldeci Paraguassu Feio |
Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em FÃsica, UFC, BR |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0144 seconds