Intensive research on development of alternative low cost, high temperature membranes for proton exchange membrane (PEM) fuel cells is going on because of the well-known limitations of industry standard perfluoro-sulfonic acid (PFSA) membranes. To overcome these limitations such as the decrease in performance at high temperatures (> / 80 0C) and high cost, non-fluorinated aromatic hydrocarbon based polymers are attractive. The objective of this study is to develop alternative membranes that possess comparable properties with PFSA membranes at a lower cost. For this purpose post-sulfonation studies of commercially available engineering thermoplastics, polyether-ether ketone (PEEK) and polyether-sulfone (PES), were performed by using suitable sulfonating agents and conditions. Post sulfonated polymers were characterized with proton nuclear magnetic resonance spectroscopy (H+-NMR), sulfur elemental analysis and titration to calculate the degree of sulfonation (DS) values and with TGA and DSC for thermal stability and glass transition temperature (Tg). Chemical stabilities were evaluated by hydrogen
v
peroxide tests. Proton conductivities of sulfonated PEEK (SPEEK) measured by electrochemical impedance spectroscopy (EIS) were observed to increase linearly with degree of sulfonation (DS). However, above a certain DS SPEEK loses its mechanical stability significantly with excessive swelling which leads to deteriorations in mechanical stability. Therefore, DS of 50-70% were used for the fabrication of composite membranes. To improve mechanical stability, SPEEK polymers were blended with more stable polymers, polyether-sulfone (PES) or in its sulfonated form (SPES) or with polybenzimidazole (PBI). In addition, the composite approach, which involves the incorporation of various inorganic fillers such as zeolite beta, TiO2, montmorrilonite (MMT), heteropolyacids (HPA), was used for further improvement of proton conductivity. Among the composite membranes 20% TPA/SPEEK (DS=68) composites conductivity value exceeded that of Nafion&lsquo / s at room temperature. Effects of various parameters during the fabrication process such as the filler type and loading, DS of sulfonated polymer, casting solvents, and thermal and chemical treatment were also investigated and optimized. Various blend/composite membranes were fabricated with solvent casting method, and characterized for their proton conductivity, chemical/thermal stability and for evaluating their voltage/current performance at various temperatures in a single cell setup. Chemically and thermo-hydrolytically stable composite/blend membranes such as 25% tungstophosphoric acid (TPA)/PBI(5%)/SPEEK (DS=68) with good single cell performances at 800C were developed (~450 mA/cm2 at 0.5 V). The performance of the hydrolytically stable composite/blend membrane prepared with SPEEK (DS=59) / 5% PBI / and 10% TiO2 increased appreciably when the temperature was raised from 80 0C to 90 0C while the performance of Nafion decreases sharply after 80 0C.
Methanol permeability studies were also performed for investigating the potential of fabricated blend/composite membranes for direct methanol fuel cell (DMFC) use. Selectivities (conductivity/methanol permeability)
vi
greater than Nafion 112 (S=7.3x107) for DMFC were observed for composite/blend membranes such as 10% TiO2/10% PES blend with SPEEK (DS=68) with a selectivity of 9.3x107. The factors that affect proton conductivity measurements were investigated and equivalent circuit analysis was performed with results obtained by electrochemical impedance spectroscopy (EIS). The choice of the conductivity cell (electrodes, cell geometry) and the method (2-probe vs 4-probe) were shown to affect the conductivity analysis. A systematic development and characterization route was established and it was shown that by optimizing proton conductivity and thermal/chemical stability with blending/composite approaches it is possible to produce novel high performance proton exchange membranes for fuel cell applications.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12609387/index.pdf |
| Date | 01 February 2008 |
| Creators | Akay, Ramiz Gultekin |
| Contributors | Bac, Nurcan |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | Ph.D. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.002 seconds