Objective: Compare in vitro the microhardness of two composites resins (Filtek ™ Z 350xt and Tetric® N-Ceram) immersed in an isotonic drink (Gatorade®) and an energy drink (Red Bull ®). Materials and methods: The study was experimental in vitro. 44 composite resin blocks were prepared, which were divided into two groups according to trademark and, within these, by type of sports drink 11 specimens used to drink Gatorade® and Red Bull®. Resin blocks were stored in distilled water in an oven at 37 ° C. Initial microhardness was measured at 24 hours of ready-made. Subsequently, they were immersed in energy drinks for 10 minutes daily for 5 days and then proceeded to measure the final microhardness through the Vickers microdurometer. Results: An initial average 77.73 + 4.34 and 3.93 73.73+, and a final average of 54.27 + 4.29 and 3.59 52.64+ for Tetric® N-Ceram resin was found after being submerged to drink Red Bull® and Gatorade® respectively. Also, an initial average of 92.91 + 4.78 and 92.27+ 2.65, and a final average of 80.55 + 4.03 and 3.46 for 80+ Filtek ™ Z 350xt after immersion to the same drinks resin was found. In addition, statistically significant differences were found when comparing the surface microhardness of composite resins before and after immersing in beverages obtaining a p= 0.000. On the other hand, no statistically significant differences were found when comparing the decrease of microhardness of resins versus energy drinks. However, when comparing the two brands of composite resin statistically significant differences (p = 0.000) were seen. Conclusions: The decrease in surface microhardness of Filtek ™ Z xt 350 resin after being submerged for drinks Gatorade® and Red Bull® was lower compared to Tetric® N-Ceram resin. / Objetivo: Comparar in vitro la microdureza superficial de dos resinas compuestas (Filtek™ Z 350xt y Tetric® N-Ceram) sumergidas en una bebida isotónica (Gatorade®) y una bebida energizante (Red Bull®). Materiales y métodos: El estudio fue experimental in vitro. Se confeccionaron 44 bloques de resina compuesta, los cuales se dividieron en dos grupos según marca y, dentro de estos, según tipo de bebida isotónica y energizante para lo que se utilizó 11 especímenes para la bebida Gatorade® y Red Bull®. Los bloques de resina estuvieron almacenados en agua destilada en una estufa a 37° C. Se midió la microdureza inicial a las 24 horas de confeccionadas las muestras. Posteriormente, se sumergieron en las bebidas isotónicas por 10 minutos diarios durante 5 días y luego se procedió a medir la microdureza final a través del microdurómetro de Vickers. Resultados: Se encontró una media inicial de 77.73 + 4.34 y de 73.73+ 3.93, y una media final de 54.27 + 4.29 y 52.64+ 3.59 para la resina Tetric® N-Ceram luego de ser sumergida a la bebida Red Bull® y Gatorade® respectivamente. Asimismo, se encontró una media inicial de 92.91 + 4.78 y 92.27+ 2.65, y una media final de 80.55 + 4.03 y 80+ 3.46 para la resina Filtek™ Z 350xt luego de su inmersión a las mismas bebidas. Además, se encontraron diferencias estadísticamente significativas al comparar la microdureza superficial de las resinas compuestas, antes y después de sumergirlas en las bebidas (p=0.000). Por otro lado, no se encontraron diferencias estadísticamente significativas al comparar la disminución que generan ambas bebidas. Sin embargo, al comparar las dos marcas de resina compuesta se observaron diferencias estadísticamente significativas (p=0.000). Conclusiones: La disminución de la microdureza superficial de la resina Filtek™ Z 350 xt luego de ser sumergida a las bebidas Gatorade® y Red Bull® fue menor si se la compara con la resina Tetric® N- Ceram. / Tesis
| Identifer | oai:union.ndltd.org:PERUUPC/oai:repositorioacademico.upc.edu.pe:10757/581918 |
| Date | 11 July 2015 |
| Creators | Castilla Minaya, Olga |
| Contributors | Hermoza Novoa, Mónica Mercedes |
| Publisher | Universidad Peruana de Ciencias Aplicadas (UPC), PE |
| Source Sets | Universidad Peruana de Ciencias Aplicadas (UPC) |
| Language | Spanish |
| Detected Language | English |
| Type | info:eu-repo/semantics/bachelorThesis |
| Format | application/pdf, application/msword |
| Source | Universidad Peruana de Ciencias Aplicadas (UPC), Repositorio Académico UPC |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Poggio C, Lombardi M, Gaviati S, Chiesa M. Evaluation of Vickers hardness and depth of cure of six composite resins photo- activated with different polymerization modes. J Conserv Dent 2012; 15(3): 237- 41. 2. Yaman B, Efes B, Dörter C, Gömeç Y, Erdilek D, Büyükgökçesu S. The effects of halogen and light- emitting diode light curing on the depth of cure and surface microhardness of composite resin. J Conserv Dent 2011; 14(2): 136- 9. 3. Nevárez R, González L, Ceballos G, Orrantia B, Makita A, Nevárez R. Influencia de la humedad sobre las resinas compuestas de uso odontológico. Rev UACh 2008; 45: 1- 10. 4. Rodríguez D, Pereira N. Evolución y tendencias actuales en resinas compuestas. Acta Odontol Venez 2008; 46: 3. 5. Jyothi KN, Shanol C, Venugopal P. Effect of five commercial mouth rinses on the microhardness of a nanofilled resin composite restorative material: An in vitro study. J Conserv Dent 2012; 15(3): 214- 17. 6. Gómez S, Noriega M, Guerrero J, Borges A. Evaluación in vitro de la microdureza superficial de diferentes resinas comerciales, frente a la acción de una bebida gaseosa. Rev Odont Mex 2010; 14(1): 8- 14. 7. Lima I, Mendes J, Sousa C, Machado L, Miranda E, Célia R. Effects of heat treatment on the microhardness of direct composites at different depths of restoration. Rev Odonto Cienc1 2012; 27(1): 36- 40. 8. Michue M. Degradación superficial provocada por una bebida de pH ácido sobre bloques de composite de nanorrelleno comparado con composite mini- híbrido. Tesis para licenciatura. Universidad Nacional Federico Villarreal; 2010. 9. Gill P. Comparative Evaluation of the effect of topical fluorides on the microhardness of various restorative materials: An in vitro study. J Indian Soc of Pedod and Prev Dent 2010; 28(3): 193- 9. 10. Lovell L, Lu H, Elliott J, Stansbury W, Bowman C. The effect of cure rate on the mechanical properties of dental resins. J Acad of Dent Mater 2001; 17: 504- 11. 11. Liñan C, Meneses A, Delgado L. Evaluación in vitro del efecto erosivo de tres bebidas carbonatadas sobre la superficie del esmalte dental. Rev Estomatol Herediana 2007; 17(2): 58- 62. 12. Adem K, Tamer T, Mustafa U, Baris K, Onur S. Conversion degree, microhardness, microleakage and fluoride release of different fissure sealants. J Mech Behav Biomed Mater. 2010; 3(8): 594-9. 13. Santini A, Miletic V, Swift M, Bradley M. Degree of conversion and microhardness of TPO-containing resin-based composites cured by polywave and monowave LED units. J Dent 2012; 40(7): 577- 84. 14. Hervás A, Martínez M, Cabanes J, Barjau A, Fos P. Resinas compuestas. Revisión de los materiales e indicaciones clínicas. J Med Oral Patol Oral Cir Bucal 2006; 11: E215- 20. 15. López O, Cerezo Correa M. Potencial erosivo de las bebidas industriales sobre el esmalte dental. Rev Cubana Salud Pública 2008; 34(4). 16. Mas C. Efecto erosivo valorado a través de la microdureza superficial del esmalte dentario, producido por tres bebidas industrializadas de alto consumo en la ciudad de Lima. Estudio in vitro. Tesis para licenciatura. Universidad Nacional Mayor de San Marcos; 2002. 17. Palma R, Elias A, Matson E, Chinelatti M, Pereira R. Microhardness of Esthetic Restorative Materials of Different Depths. Materials Research 2002; 6(1): 85- 90. 18. Santos E, Yenque J, Rojas O, Rosales V. Notas Científicas Acerca del Ensayo de Dureza. Industrial Data 2001; 4(2): 73- 80. 19. Moreno X, Narváez C, Bittner V. Efecto in vitro de las Bebidas refrescantes sobre la Mineralización de la Superficie del Esmalte Dentario de Piezas Permanentes Extraídas. Int J Odontostomat 2011; 5(2): 157- 63. 20. Álvarez C, Carrillo J, Calatayud J, Carrillo I, Latorre R. Análisis comparativo de la microdureza Rockwell superficial y Vickers en diferentes composites con esmalte y dentina natural. Rev UEM 2001. 21. Fernández N, Fernández D, Coelho F, Klein C, Maciel L, Galia E. Análisis comparativo de la microdureza superficial de dos resinas compuestas sometidas a complementación de polimerización. Rev Asoc Odont Rest y Biom 2005; 3(1). 22. Bayne S. Dental Biomaterials: Where are we and Where are we going? J Dent Educ 2005; 69(5): 571- 85. 23. Soto J, Lafuente D. Efectos de las bebidas gaseosas sobre algunas resinas compuestas. Rev Cient Odontol 2013; 9(2): 9-15. 24. Mahan LK, Escott S. Nutrición para el rendimiento en el ejercicio y los deportes. Krause. Dietoterapia 2009; Elsevier-Masson, Edición 12: 598-9. 25. Williams MH. En Minerales: Los reguladores inorgánicos. Nutrición para la salud, condición física y deporte 2006; Mc Graw Hill: 293-330. 26. Jara L, Matos A. Bebidas energéticas: desarrollo en la industria de alimentos y mercado nacional. Ponencia presentada en el I Congreso Nacional de Investigación. 2011- Lima. 27. Klepacki B. Energy Drinks: A Review Article. Strength Cond J 2010; 32(1):37-41. 28. Tauquino JF. Evaluación in vitro de la microdureza superficial de una resina compuesta microhíbrida, una resina compuesta fluida y un cemento ionómero vítreo de restauración frente a la acción de una bebida carbonatada. Tesis para licenciatura. Universidad Nacional Mayor de San Marcos; 2002. 29. Leite B. Influència de bebidas ácidas sobre resina composta nanohíbrida. Tesis para licenciatura. Universidade Estadual da Paraíba; 2014. 30. Nazish F, Mehwish H. Effect of two different commonly available energy drinks on surface microhardness of tooth color restorative materials. J Research Dent 2014; 2 (3): 269- 76. 31. Tanthanuch S, Kukiattrakoon B, Siriporananon C, Ornprasert N, Mettasitthikorn W, Likhitpreeda S, Waewsanga S. The effect of different beverages on surface hardness of nanohybrid resin composite and giomer. J Conserv Dent 2014;17: 261-5. 32. Nainan MT, Balan AK, Sharma R, Thomas SS, Deveerappa SB. The comparison of the effects of different whitening toothpastes on the micro hardness of a nano hybrid composite resin. J Conserv Dent 2014;17:550-9 33. Erdemir U, Yildiz E, Mert Eren M, Ozel S. Surface hardness evaluation of different composite resin materials: influence of sports and energy drinks immersion after a short-term period. J. Appl. Oral Sci. 2013; 21 (2). 34. Revilla M. Microdureza superficial in vitro de resinas de nanotecnología, frente a la acción de dos bebidas carbonatadas. Tesis de licenciatura. Universidad Nacional Mayor de San Marcos; 2011. 35. Moroz T, Alves L, Luciano M, Luiz G, Kossatz S. Influência de substâncias com pH ácido sobre a microdureza de resinas compostas. Rev Stomatos 2010; 16(30): 21- 32. 36. Araújo J. Análise da microdureza de resinas compostas expostas a repositores hidroeletrolìticos. Tesis para licenciatura. Universidade Federal da Paraíba; 2010. 37. Câmara D, Robeiro G, Rondon P, Carneiro M, Gomes C, Máximo MA. Evaluation of Compressive Strength and Microhardness of composites associated to Light Curing Characterizing Materials. World J Dent 2014; 5(1): 6- 10. 38. Suarez R, Lozano F. Comparación de la dureza superficial de resinas de nanotecnología, según el momento del pulido: in vitro. Rev Estomatol Herediana 2014; 24(1):11-6. 39. Naranjo R, Lince J, Vivas J, Ortiz P. Diferencia en la dureza de resinas utilizadas convencionalmente al polimerizarse con diferentes tipos de luz. Rev U CES 2014; 1- 22. 40. Yap AU, Tan CH, Chung SM. Wear behavior of new composite restoratives. Oper Dent 2004; 29(3): 269- 74. 41. Abu- Naila A, Baban L. The effect of cyclic immersion in cola drinks on the surface microhardness and surface roughness of different composite filling resin materials. J Bagh Coll Dent. 2010; 22(2): 7- 11. 42. Hengtrakoola CH, Kukiattrakoonb B, Kedjarune-Leggatc U. Effect of Naturally Acidic Agents on Microhardness and Surface Micromorphology of Restorative Materials. Europ J Dent. 2011; 5: 89- 100. 43. Galdino E. Tesis para licenciatura. Universidade Federal da Paraíba; 2010. Tesis para licenciatura. Universidade Federal da Paraíba; 2013. 44. Cao L, Zhao X, Gong X, Zhao S. An in vitro investigation of wear resistance and hardness of composite resins. Int J Clin Exp Med. 2013; 6 (6): 423- 30. 45. Valinoti A, Neves B, Silva E, Maia L. Surface degradation of composite resins by acidic medicines and pH- cycling. J Appl Oral Sci. 2008; 16(4): 257- 65. |