Previous issue date: 2016-01-29 / CNPq / A busca por combustíveis limpos tem resultado no desenvolvimento de pesquisas
para o beneficiamento de óleos e gorduras, constituídos principalmente por ácidos
graxos, com alto poder energético e passível de conversão em ésteres (biodiesel),
mediante reações de transesterificação e esterificação com catálise homogênea,
heterogênea e enzimática. Os problemas identificados no uso de esterificação com
catálise homogênea podem ser minimizados pela esterificação com catálise
heterogênea, que busca melhorar a efetividade da produção do biodiesel. Nesse
estudo o catalisador heterogêneo desenvolvido é conhecido por ferritas, que são
materiais ferrimagnéticos que vem sendo alvo de inúmeras pesquisas científicas em
virtude das suas propriedades magnéticas, estabilidade química e térmica. Assim,
uma aplicação que tem apresentado promissora para esses materiais é a área de
catálise para o biodiesel. Com base neste contexto, esta pesquisa propôs sintetizar
nanoferritas Ni1-xZnxFe2O4 (x = 0,0; 0,3; 0,5; 0,7 e 1,0 mol de Zn2+) por reação de
combustão e avaliar a influência da substituição dos íons Ni2+por íons Zn2+na estrutura, morfologia e atividade catalítica em reação de esterificação do óleo de
soja em presença de metanol. Durante a síntese foi realizada a medição do tempo e
temperatura de chama e os produtos resultantes foram caracterizados por difração
de raios X, fluorescência de raios X por energia dispersiva, análise textural por
adsorção de N2, espectroscopia na região do infravermelho com transformada de
Fourier, distribuição granulométrica, densidade, microscopia eletrônica de varredura,
análise termogravimétrica e medidas magnéticas. O biodiesel obtido foi analisado
por um cromatógrafo a gás. Para esse fim, uma investigação da dependência da
morfologia, magnetismo, acidez e atividade catalítica dos nanocatalisadores foram
avaliados em função do teor de Zn2+. O aumento do teor de Zn2+causou alterações
na estrutura, morfologia, magnetismo, acidez e potencial zeta das amostras, o que
contribuiu significativamente para o aumento na conversão catalítica, a qual variou
de 49,08% a 99,06%. Os resultados indicam que os nanocatalisadores Ni1-xZnxFe2O4 são materiais promissores para uso em reações de esterificação para
produção de biodiesel. / The search for clean fuels has resulted in the development of research for the
processing of fats and oils mainly consisting of fatty acids, high-energy power which
can be converted to esters (biodiesel) by trans-esterification reactions and
esterification with homogeneous catalysis, heterogeneous and enzyme. The
problems identified with the use of esterification with homogeneous catalysis can be
minimized by esterification with heterogeneous catalysis that seeks to improve the
effectiveness of the production of biodiesel. In this study the heterogeneous catalyst
developed it is itself known as ferrites which are ferromagnetic materials that have
been the subject of numerous scientific studies due to their magnetic properties,
chemical and thermal stability. Therefore, an application that has shown promise for
these materials is the catalysis for biodiesel. Based on this background the present
study concerns itself to synthesize nanoferrites Ni1-xZnxFe2O4 (x = 0.0; 0.3; 0.5; 0.7
and 1.0 mol of Zn2+) by combustion reaction to evaluate the influence of replacement
of the Ni2+ions by Zn2+ions in the structure, morphology, and catalytic activity in
soybean oil esterification reactions in the presence of methanol. In order to find out
what was really happening, during the research the time measurement and flame
temperature and the resulting product was characterized by X-ray diffraction, X-ray
fluorescence energy dispersive, textural analysis by N2 adsorption spectroscopy in
the infrared Fourier transform, particle size distribution, density, scanning electron
microscopy, thermal analysis and magnetic measurements. The biodiesel obtained
was analysed by a gas chromatograph. It was noticed that, an investigation of the
dependence of morphology, magnetism, acidity and catalytic activity of the
nanocatalyst were evaluated according to the Zn2+content. The findings reflected
that, the increase of the Zn2+content caused changes in the structure, morphology,
magnetism, acidity and zeta potential of the samples, which contributed significantly
to the increase in the catalytic conversion, which ranged from 49.08% to 99.06%. It
was found out that Ni1-xZnxFe2O4 nanocatalysts are promising materials for use in
the esterification reaction for biodiesel production.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1267 |
| Date | 26 July 2018 |
| Creators | MAPOSSA, António Benjamim. |
| Contributors | COSTA, Ana Cristina Figueiredo de Melo., FREITAS, Normanda Lino de., SILVA, Adriano Sant´Ana da., PEREIRA, Kleberson Ricardo de Oliveira., OLIVEIRA, Djane de Fátima. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds