Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T02:04:38Z (GMT). No. of bitstreams: 1
DiFrancescantonio_Marina_M.pdf: 16720831 bytes, checksum: ce2d1ee161bca05d6b15b3e0a9eaeedd (MD5)
Previous issue date: 2009 / Resumo: As propriedades mecânicas dos cimentos resinosos são influenciadas pelo tipo e
composição da matriz resinosa, tipo e tamanho das partículas de carga, modo e
grau de conversão dos monômeros em polímeros, e a viscosidade é uma
propriedade que está intimamente ligada a esses fatores. Os objetivos deste
estudo foram avaliar a influência da viscosidade (alta e baixa) e modo de
polimerização (polimerização dual e autopolimerizado) de cimentos resinosos
duais (Nexus 2/ Kerr, Corp e Variolink II/ Ivoclar-Vivadent): na resistência de união
da restauração à dentina (RU), no grau de conversão (GC) e na resistência
flexural biaxial (RFB). Para o teste de RU, substratos dentinários de cinqüenta e
seis terceiros molares humanos foram utilizados para o ensaio de microtração
através da cimentação de uma peça protética do material de resina composta
indireta e estes foram foto-ativados ou não segundo cada grupo experimental.
Após 24 horas, os dentes foram secionados para obter espécimes em forma de
palitos (de área de secção transversal de 1.0 mm²), que foram testados em tração
a uma velocidade de 0,5 mm/ mim (4411/Instron). Os resultados foram analisados
por ANOVA 3 fatores e teste Tukey (p=0,05). Para a análise do GC, os cimentos
foram aplicados na superfície da unidade de reflectância total atenuada acoplada
ao espectrômetro infravermelho (Nicolet Instrument Corp, Madson, Wisconsin,
EUA) sendo foto-ativados ou não. Espectros foram obtidos após 5 minutos e 24
horas. O cálculo do grau de conversão foi realizado através da análise da
mudança na proporção entre as alturas dos picos das ligações duplas de carbono
alifática e aromática. Os dados foram submetidos a ANOVA 3 fatores e teste de
Tukey (p=0,05). Para o ensaio de RFB, noventa e seis discos de cimentos
resinosos (0,5mm de espessura/ 6mm de diâmetro) foram preparados utilizando
moldes de silicone de adição (n=12) e foram foto-ativados ou não segundo os
grupos experimentais. Após 5 dias, os discos foram testados em dispositivos de
ensaio de flexão biaxial em máquina de ensaio universal (1,27 mm/min, Instron
5844) e os dados analisados estatisticamente por ANOVA 3 fatores e teste Tukey(p=0,05). Para a RU, a polimerização dual (foto + autopolimerização) aumentou
significantemente os valores médios para os cimentos resinosos em baixa
viscosidade para ambos os cimentos resinosos duais utilizados no estudo. Em
relação o GC, a foto-ativação e quando o GC foi mensurado após 24 horas,
aumentaram significativamente o GC para ambos os cimentos resinosos. A versão
em baixa viscosidade apresentou maior GC que os em alta viscosidade, para as
duas formas de polimerização. No teste RFB, a foto-ativação aumentou
significantemente a resistência e módulo de flexão. A versão em alta viscosidade
quando foto-ativada mostrou maior resistência flexural que em baixa viscosidade,
enquanto a viscosidade não alterou os valores médios de módulo flexural. Pode-se
concluir que a foto-ativação é necessária durante a cimentação de restaurações
indiretas, para garantir adequadas propriedades físico-químicas, e a utilização de
cimentos resinosos em diferentes viscosidades pode modificar os valores médios
de RFB, GC e RU à dentina. / Abstract: The mechanical properties of resin cements may be influenced by the type and
monomer composition, type and filler size, mode, and degree of conversion, which
are all associated with resin viscosities. The aim of this study was to evaluate the
influence of resin cement viscosity (high and low) (Nexus 2/ Kerr, Corp and
Variolink II/ Ivoclar-Vivadent) and the curing mode (dual and chemical activation)
on the bond strength to dentin, on the degree of conversion and biaxial flexural
strength. For microtensile bond strength test, two bonding agents and their
respective resin cement, occlusal dentin surfaces of fifty-six human third molars
were used for the testing and the resin cements were applied to pre-cured resin
composite discs, which were fixed to dentin surfaces, simulating an indirect
restoration. The restored teeth were either light-activated or allowed to self-cure,
according to experimental groups. After 24 hs, the teeth were sectioned to obtain
bonded beams specimens (1.0 mm²). Each specimen was tested in tension at a
crosshead speed of 0.5 mm/min (4411/Instron). Data (MPa) was analyzed by 3-
way ANOVA and Tukey's Tukey's test (p=0.05). To evaluate the degree of
conversion, the resin cements were applied to surface of a horizontal attenuatedtotal-
reflectance unit (Nicolet Instrument Corp, Madson, Wisconsin, EUA) and were
polymerized using one of two conditions: self-cure (SC) or direct light exposure
(600 mW/cm2, XL3000/3M ESPE) and infrared spectra were obtained after 5
minutes and 24 hours. The degree of conversion was calculated using standard
techniques of observing changes in aliphatic-to-aromatic peak ratios pre- and postcuring.
Data were analyzed by 3-way repeated measure ANOVA and Tukey's test
(p=0.05). For the biaxial flexural strength, forty-eight resin cement discs of each
product (0.5 mm thick and 6.0 mm in diameter) were created using silicon
impression material molds (n=12) and were either light activated or not, according
to experimental groups. After 5 days, the specimens were subjected to the biaxial
flexure test in a universal testing machine (1.27 mm/min, Instron 5844) and the
data ware statistically analyzed by 3-way ANOVA and Tukey's post-hoc test (p=0.05). For bond strength testing, the dual curing mode increased the bond
strength for the low viscosity resin cements for both dual resin cement used in this
study. For the degree of conversion, the light activation, after 24h, significantly
increased the degree of conversion for both resin cements, and the low viscosity
version from dual cure or self-cured groups exhibited higher degree of conversion
than high viscosity version. Regarding biaxial flexural strength, the light-activation
significantly increased flexural strength and modulus, and the high viscosity
versions of dual cure groups exhibited higher flexural strength than their low
viscosity versions, while the viscosity of resin cements did not influence the
modulus. In conclusion, the light-activation of dual resin cements is required in
indirect restorations, to provide proper mechanical and chemical properties, and
the use of resin cements with different viscosities may change the bonding
biomechanical characteristics of indirect restorations. / Mestrado / Dentística / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/287817 |
| Date | 13 August 2018 |
| Creators | Di Francescantonio, Marina |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Giannini, Marcelo, 1969-, Braga, Roberto Ruggiero, Sinhoreti, Mário Alexandre Coelho |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 85f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0028 seconds