Orientador: Altair A. Del Bel Cury / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-25T05:46:32Z (GMT). No. of bitstreams: 1
Mello_JoseAntonioNunesde_M.pdf: 3694563 bytes, checksum: beacf7b79afd8dcaa091933c87f0830e (MD5)
Previous issue date: 1999 / Resumo: o monômero residual em excesso pode causar reações inflamatórias na mucosa além de alterar as propriedades mecânicas da resina. O objetivo desse estudo foi avaliar o efeito do aquecimento pelas microondas e água quente no nível de monômero residual de uma resina acrílica autopolimerizável e polida quimicamente e sua influência na resistência transversa e na microdureza interna. Quatro grupos com amostras específicas para cada ensaio foram confeccionados com resina autopolimerizáve1 JET CLÁSSICO. Gl) as amostras foram submetidas ao polimento mecânico; G2) as amostras foram submetidas ao polimento químico com fluído para polimento POLI-QUIM; G3) após o polimento químico, as amostras foram submetidas a um ciclo complementar de polimerização no microondas de 450 W / 3 min e G4) após o polimento químico, as amostras receberam um ciclo complementar em água a 65°C / 1 h. As médias e desvios padrões da liberação de monômero na água no 1° dia em Ilg / cm2 foram: Gl=136,65:t 45,56 (a); G2=1315,70:t 225,50 (b); G3=848,21 :t 150,46 (c) e G4=295,18:t 81,67 (a). As médias e desvios padrões da resistência transversa em MPa foram: Gl=78,15 :t 6,11 (a); G2=65,15 :t 7,79 (b); G3=70,48 :t 2,96 (b) e G4=67,54 :t 8,05 (b). As médias e desvios padrões da microdureza interna (Knoop) foram: em 100 !lm - Gl=14,71 :t 1,07 (a); G2=12,79 :t 1,54 (a); G3=12,90:t 1,07 (a) e G4=11,69:t 2.51 (a); em 700 !lm - Gl=16,04:t 0,96 (a); G2=15,43 :t 0,69 (a); G3=15,31 :t 0,74 (a) e G4=18,07:t 0,53 (b); em 1500 !lm - Gl=16,21 :t 1,40 (a); G2=15,83 :t 0,70 (a); G3=15,56 :t 0,72 (a) e G4=18,85 :t 0,73 (b). A análise de variância e a comparação utilizando o teste de Tukey mostrou diferença entre os grupos e as médias seguidas por letras diferentes mostraram diferença significativa (a=5%). Diante desses resultados conclui-se que: o polimento químico aumentou o nível de monômero residual, diminuiu a resistência transversa das resinas e não alterou os valores de microdureza interna. As microondas e a água quente podem
ser usados para reduzir os níveis de monômero residual no primeiro dia após a polimerização / Abstract: The monomeric methyl methacrylate can cause tissue damage. The aim of the present study was to investigate the effect of microwave heating and hot water on the residual monomer levei of an acrylic resin chemicaly activated and chemicaly polished and their effects on the transverse strength and internal microhardness. F our groups with specific patterns to each test were prepared using JET CLASSICO, an autopolimering resin. G 1) the specimens were mechanicalypolished; G2) the specimens were chemicaly polished using POLI-QUIM, a chemical polishing fluid; G3) after the chemical polishing, the specimens were submited to an aditional cicIe in the microwave oven irradiated at 450 Watts for 3 minutes; G4) after the chemical polishing, the specimens were submited to an aditional cicIe into water at 65°C for 1 hour. The means and standard deviations of residual monomer lost into water at the 1 st day were (flglcnf): Gl=136.65 :t 45.56 (a), G2=1315.70 :t 225.50 (b), G3=848.21 :t 150.46 (c) e G4=295.18:t 81.67 (a). The means and standard deviations oftransverse strength were (MPa): Gl=78.15.:t 6.11 (a), G2=65.15 :t 7.79 (b), G3=70.48 :t 2.96 (b) e G4=67.54 :t 8.05 (b). The means and standard deviations ofinternal microhardness were (Knoop): at 100 flm - Gl=14.71 :t 1.07 (a), G2=12.79 :t 1.54 (a), G3=12.90 :t 1.07 (a) e G4=11.69 :t 2.51 (a); at 700 flm Gl=16.04:t 0.96 (a), G2=15.43 :t 0.69 (a), G3=15.31 :t 0.74 (a) e G4=18.07:t 0.53 (b); ~t 1500 flm - Gl=16.21 :t 1.40 (a), G2=15.83 :t 0.70 (a), G3=15.56:t 0.72 (a) e G4=18.85 :t 0.73 (b). The results of anlysis of variance and the means comparison using Tukey test showed diference between the groups. The means folowed by diferent letters showed significant diference (a=5%). It was conclude that: quimical polishing increased the leveI of residual monomer; decreased the transverse strength of acrylics; did not change the values of internal microhardness; microwave and hot water can be used to reduce the levei of residual monomer at the 1st day / Mestrado / Protese / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290283 |
| Date | 23 June 1999 |
| Creators | Mello, Jose Antonio Nunes de |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Del Bel Cury, Altair Antoninha, 1948-, Ribeiro, Fernando da Cunha, Henriques, Guilherme Elias Pessanha |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 91p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0026 seconds