Previous issue date: 2018-03-26 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A construção civil é uma importante indústria no sistema econômico em que está
inserida. Além de gerar emprego e renda, o setor também contribui modificando o
cenário natural para garantir à sociedade moradia, segurança e bem-estar. No
entanto, os altos índices de recursos naturais utilizados pela construção, bem como
as grandes quantidades de resíduos gerados por ela, trazem grande preocupação
referente ao impacto ambiental negativo gerado e as suas consequências. Tendo
em vista o alto consumo energético no processo de fabricação do cimento, as
grandes quantidades de CO2 emitidas durante a queima do clínquer, a
disponibilidade de cal hidratada na região Nordeste do Brasil e ainda, o alto índice
de perdas que envolve os blocos cerâmicos utilizados em alvenarias de vedação,
esse trabalho avaliou o potencial de substituição do cimento pela cal em tijolos de
solo-cimento com incorporação de resíduo cerâmico (RC). Foram desenvolvidas
composições ternárias de solo + 12% cimento + 4% RC, solo + 12% cal hidratada +
4% RC, quaternárias de solo + 6% cimento + 6% cal hidratada + 4% RC. As
composições também foram formuladas sem adição de RC para servirem como
referência e possibilitar a análise da influência do resíduo sobre o comportamento
dos tijolos produzidos. Após os processos de prensagem e cura dos tijolos, estes
foram submetidos a ensaios de resistência mecânica, absorção de água e
durabilidade modificada. Em seguida, analisou-se a microestrutura desses materiais
através de Microscopia Eletrônica de Varredura (MEV) e Difração de raios X (DRX)
das superfícies de fratura. Dados os teores de sílica e alumina presentes, tanto no
solo empregado, como no resíduo cerâmico finamente moído, pode ocorrer a reação pozolânica que, por sua vez, contribui para a melhoria das propriedades físicas e
mecânicas das composições estudadas. Observou-se que os tijolos produzidos
apresentaram boas condições de resistência a compressão simples, absorção de
água e durabilidade em acordo com recomendações das Normas vigentes para
tijolos em aplicação não estrutural. Os resultados experimentais constataram que a
composição ternária solo + 12% cimento + 4% RC apresentou valores mais
significativos, ultrapassando 2 Mpa de resistência à compressão simples, a partir dos
150 dias de cura. Entre as misturas quaternárias, a formulação solo + 6% cimento +
6% cal e 4% RC apresentou o melhor desempenho, superando a resistência à
compressão mínima de 2 MPa recomendada pela Norma, a partir dos 120 dias de
cura. Com base nos resultados obtidos é possível concluir que, tanto do ponto de
vista técnico, como econômico, a substituição do cimento pela cal em tijolos de solocimento,
é viável, com os benefícios da incorporação do RC e observando-se os
tempos de cura necessários para a efetiva hidratação dos aglomerantes e das
reações pozolânicas. / Civil construction is an important industry in the economic system in which it is
inserted. In addition to generating employment and income, the sector also
contributes by modifying the natural landscape to guarantee society housing, security
and well-being. However, the high indices of natural resources used by the
construction, as well as the large amounts of waste generated by it, raise great
concern about the negative environmental impact generated and the serious
consequences. Considering the high energy consumption in the cement
manufacturing process, the large amounts of CO2 emitted during clinker firing, the
availability of hydrated lime in the Northeast region of Brazil, and also the high loss
rate involving the ceramic blocks used in sealing masonry, this work evaluated the
potential of cement substitution by lime in soil-cement bricks with ceramic residue
(RC) incorporation. Ternary compositions of soil + 12% cement + 4% CR, soil + 12%
hydrated lime + 4% CR, quaternary soil + 6% cement + 6% hydrated lime + 4% CR
were developed. The compositions were also formulated without addition of RC to
serve as reference and enable the analysis of the influence of the residue on the
behavior of the bricks produced. After the pressing and curing processes of the
bricks, they were submitted to tests of mechanical resistance, water absorption and
modified durability. Then, the microstructure of these materials was analyzed through
Scanning Electron Microscopy (SEM) and X-ray Diffraction (XRD) of the fracture surfaces. Given the silica and alumina contents present in both the used soil and the
finely ground ceramic residue, the so-called pozzolanic reaction occurs, that
contribute to the improvement of the physical and mechanical properties of the
compositions studied. It was observed that the bricks produced presented good
conditions of resistance to simple compression, water absorption and durability in
accordance with the recommendations of the current Standards for bricks in nonstructural
application. The experimental results showed that the ternary composition
soil + 12% cement + 4% CR showed more significant values, exceeding 2 MPa of
simple compression strength, after 150 days of cure. Among the quaternary mixtures,
the soil formulation + 6% cement + 6% lime and 4% CR showed the best
performance, exceeding the minimum compression strength of 2 MPa recommended
by Norma, after 120 days of cure. Based on the results obtained, it is possible to
conclude that, from a technical and economic point of view, the replacement of
cement by lime in soil-cement bricks is viable, with the benefits of incorporating RC
and observing the necessary for the effective hydration of the binders and the
pozzolanic reactions.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/25338 |
| Date | 26 March 2018 |
| Creators | Fonsêca, Nayara Jhéssica Marques da |
| Contributors | 50580396720, Silva, Jaqueligia Brito da, 02585622428, Nobrega, Andreza Kelly Costa, 02293726436, Silva, Vamberto Monteiro da, 67456863415, Acchar, Wilson |
| Publisher | PROGRAMA DE PÓS-GRADUAÇÃO EM ENGENHARIA CIVIL, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds