Alteração de cor e rugosidade superficial de resina composta clareada após envelhecimento em função do tempo / Color change and surface roughness of composite resin cleared after accelerated artificial aging as a function of time

O presente trabalho teve como objetivo analisar “in vitro” a alteração de cor e a rugosidade superficial de uma resina composta (Charisma®) submetidas a tratamento clareador com agente clareador Lase Peroxide Sensy® (CC) e grupo controle sem tratamento clareador (SCL), após envelhecimento (EAA) em função do tempo, realizando-se avaliação superficial complementar por meio de Microscopia Eletrônica de Varredura (MEV) e EDX. Os corpos-de-prova (n=15) foram confeccionados com o auxílio de uma matriz de Teflon nas dimensões de 11x2,0mm, polidos com discos Soft Lex®, na seqüência de abrasividade decrescente e armazenados em saliva artificial a 37ºC (±1ºC), até os momentos de serem submetidos aos tratamentos propostos e à realização das leituras de alteração de cor e rugosidade superficial, nos tempos: 24 horas após a confecção (T0), após envelhecimento artificial acelerado (T1), 24 horas após clareamento (T2), 7dias (T3) e 1 mês após clareamento (T4). As leituras de alteração de cor foram obtidas com o auxílio do aparelho Espectrofotômetro (PCB6807BYK GARDNER) e para as leituras de rugosidade superfícial foi utilizado o Rugosímetro Mitutoyo SJ201P. Os dados foram submetidos à Análise de Variância ANOVA (p≤0,05). Os resultados obtidos foram: a) o fator Tempo teve efeito estatisticamente significante sobre as variáveis ΔE* (T1=T2=T3; T1=T4), L* (T0<T1=T2=T3=T4), a* (T0>T1=T2; T1=T3=T4; T4>T2), b* (T0>T1=T2=T3; T4=T3=T1; T2<T4) e rugosidade superficial (μm) (T0<T1,T2,T3,T4; T1=T2; T1<T3=T4; T2=T3=T4; b) para o fator tratamento com relação a ΔE* e fator L*(CC>SCL), para os fatores a* e b*(CC<SC), c) a interação Tratamento x Tempo não apresentou diferença estatisticamente significante para as variáveis ΔE*, L*, a*, b* e rugosidade superficial, d) as superfícies após EAA apresentaram alterações d) não houve mudanças no EDX antes e após os tratamentos. Conclui-se que a resina Charisma®, apresentou alteração de cor (ΔE*>3,3) e uma estabilidade na rugosidade superficial a partir de T2. / The current study in vitro evaluated the color change and surface roughness of the composite resin Charisma® cleared with Lase Peroxide Sensy® (CCL) and control without bleaching (SCL) after accelerated artificial aging (EAA) as a function of time, performing additional surface evaluation by scanning electron microscopy (MEV) and EDX. To obtain the color change and surface roughness a Spectrophotometer (PCB 6807 BYK GARDNER) and rugosimeter (Mitutoyo SJ- 201P) were employed respectively. Measurements were carried out at five times: 24 hours after preparation (T0), after artificial accelerated aging (T1), 24 hours after bleaching (T2), 7days (T3) and 1 month after bleaching (T4). The specimens (n=15) were prepared with aid of a Teflon (10-mmin diameter and 2mm thick). The specimens were polished with discs Soft Lex®, following abrasiveness decreased, being stored in artificial saliva at 37ºC (±1ºC) until the time of undergoing the proposed treatments and the measurements. The data obtained were submitted to ANOVA parametric test (p ≤ 0.05). The results were: a) time factor had a statistically significant effect on the variables ΔE* (T1 = T2 = T3, T1 = T4), L*(T0 <T1 = T2 = T3 = T4), a* (T0 > T1 = T2; T1=T3 =T4, T4>T2), b* (T0> T1=T2=T3, T4=T3=T1; T2<T4) and roughness(μm) (T0<T1,T2, T3,T4; T1 = T2; T1<T3=T4; T2=T3=T4), b) for treatment factor ΔE* and L* (CC> SCL) for the factors a*and b* (CC <SC), c) Treatment x Time interaction showed no statistically significant difference for the variables ΔE*, L*, a*, b* and surface roughness, d) after EAA the surfaces change d) before and after EAA dont have changes. It is concluded that the resin Charisma®, presented color change (ΔE *> 3.3) and surface roughness stability from T2.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-19102010-085606
Date30 July 2010
CreatorsDaniela de Biagi Freitas
ContributorsAlma Blasida Concepcion Elizaur Benitez Catirse, Rosehelene Marotta Araújo, Denise Cerqueira Oliveira, Andréa Candido dos Reis, Renato Herman Sundfeld
PublisherUniversidade de São Paulo, Odontologia (Reabilitação Oral), USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds