In this study, the oxygen-deficient TiO2, SrTiO3 systems and transition metal ion (Cr or V) doped TiO2, SrTiO3 and SrZrO3 systems have been investigated. We prepared samples as polycrystals, single crystals and thin films for various desires. Their structural, physical and electronic properties were measured by bulk-sensitive techniques (X-Ray Diffraction, SQUID and Electro Paramagnetic Resonance) or surface-sensitive techniques (Photoemission spectroscopy and X-ray absorption spectroscopy). The measurement of SQUID and EPR showed not only their magnetic properties but also the valence state of Cr dopant. We verified the valence state of Cr ions in oxides and found the key parameters of sample synthesis which control the valence state of Cr ions. Segregated phases such as SrCrO4 were formed when the samples were synthesized under O2 rich environment. The surface properties of Cr doped SrZrO3 films are also discussed. We found the synthesis conditions which influence on not only the behavior of Cr ions but also the resistive-switching behaviors. Various resistive-switching behaviors seem to depend on the surface chemistry of films. We found that the accumulation of Cr3+ on film surface provides a clean interface without any non-stoichiometric oxides and that this sharp interface termination results in a good performance of resistive-switching.
Identifer | oai:union.ndltd.org:CCSD/oai:tel.archives-ouvertes.fr:tel-00856580 |
Date | 01 September 2011 |
Creators | Cho, Suyeon |
Publisher | Université Paris Sud - Paris XI |
Source Sets | CCSD theses-EN-ligne, France |
Language | English |
Detected Language | English |
Type | PhD thesis |
Page generated in 0.0014 seconds