Síntese, caracterização e avaliação reológica dos copolímeros de butadieno e estireno da série 1000 / Síntese, caracterização e avaliação reológica dos copolímeros de butadieno e estireno da série 1000 / Synthesis, characterization and rheological evaluation of the butadiene and styrene copolymers from 1000 series / Synthesis, characterization and rheological evaluation of the butadiene and styrene copolymers from 1000 series

Neste estudo foram sintetizados copolímeros de butadieno e estireno (SBR) através do processo de polimerização em emulsão a quente. Foi avaliada a influência das condições reacionais sobre as principais propriedades dos copolímeros, como grau de encolhimento no moinho, massas molares numérica média (Mn) e ponderal média (Mw), distribuição de massa molar (Mw/Mn) e propriedades reológicas das diferentes SBRs. Os copolímeros obtidos foram avaliados quanto aos módulos elástico (G) e viscoso (G) e tangente delta pelo equipamento Analisador de Processamento de Borracha (RPA) e pelo viscosímetro Mooney MV 2000. Foi verificado no copolímero obtido a influência da adição do agente de reticulação, em que pequena variação da quantidade adicionada do mesmo ao sistema de polimerização, proporcionou grande alteração nas propriedades do copolímero. Os copolímeros obtidos a diferentes conversões da reação de polimerização apresentaram aumento da viscosidade Mooney e massas molares numérica e ponderal médias com o aumento da conversão. A avaliação reológica pelo equipamento RPA de copolímeros comerciais confirmou os resultados obtidos pelo viscosímetro Mooney MV 2000 no teste de relaxação de tensão / In this study copolymers of butadiene and styrene were synthesized by a hot emulsion polymerization process. The influence of the reaction conditions was evaluated on the main properties of the copolymers, as degree of shrinkage in the mill, number (Mn) and weight-average (Mw) molecular weight, molecular weight distribution (Mw/Mn) and the rheological properties of the copolymers. The copolymers were evaluated by the elastic (G) and viscous (G) modulus and tan delta by the Rubber Process Analyser (RPA) and Mooney viscosimeter MV 2000. It was verified that the addition of small quantities of crosslinking agent in the copolymer has a higher influence on its properties. The Mooney viscosity and the number and weight-average molecular weight increased as polymerization conversion increased. The rheological evaluation by the RPA of several commercial copolymers has confirmed the results obtained by the Mooney viscosimeter MV 2000 during the stress relaxation test

Identiferoai:union.ndltd.org:IBICT/urn:repox.ist.utl.pt:UERJ:oai:www.bdtd.uerj.br:70
Date28 November 2005
CreatorsManoel Remígio dos Santos
ContributorsCristina Russi Guimarães Furtado, Fernanda Margarida Barbosa Coutinho, Regina Celia Reis Nunes
PublisherUniversidade do Estado do Rio de Janeiro, Programa de Pós-Graduação em Química, UERJ, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UERJ, instname:Universidade do Estado do Rio de Janeiro, instacron:UERJ
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0014 seconds