Previous issue date: 2016-02-16 / CNPq / As Ligas com Memória de Forma (LMF) foram descobertas nos anos 60 e o desenvolvimento de vários sistemas (NiTi, CuAlNi, CuAlBe, CuZnAl) vem sendo explorado desde então, sendo aquelas do sistema NiTi as mais utilizadas. Devido às suas excelentes propriedades mecânicas, ótima resistência a corrosão e biocompatibilidade, além de apresentarem as melhores propriedades funcionais de efeito de memória de forma e superelasticidade, as LMF NiTi e suas variações ternárias passaram a ser objeto de estudos para várias aplicações nas mais diferentes áreas. Um dos maiores problemas das LMF NiTi ainda está relacionado a dificuldades de conformação mecânica e usinagem. Por esse motivo, o processo de soldagem pode ser uma boa ferramenta alternativa para se conseguir obter peças de geometrias mais complexas, envolvendo a união das LMF NiTi com metais convencionais, como o aço inoxidável. O aço inoxidável é uma opção importante de união com LMF NiTi pois possui igualmente propriedades desejadas de resistência mecânica, biocompatibilidade e resistência a corrosão. A união por soldagem destas duas ligas encontra barreiras diversas, sendo a principal delas a formação de intermetálicos frágeis na junta soldada limitando sua resistência mecânica e consequente aplicação. Nesse contexto, o presente trabalho teve como objetivo geral avaliar a soldabilidade de chapas finas (espessura de 1 mm) de uma LMF NiTi com aço inoxidável (INOX) AISI 304 utilizando o processo micro GTAW e compreender a metalurgia da soldagem na variação das propriedades mecânicas e metalúrgicas das juntas. O processo GTAW foi escolhido por ser mais econômico que os processos usuais de soldagem para estas ligas NiTi, como a soldagem a laser (LBW). As juntas dissimilares NiTi-SS obtidas foram caracterizadas pelas técnicas de MO, MEV, EDS, DSC, ensaios de tração à ruptura e de dureza Vickers. Estas juntas foram soldadas utilizando a própria LMF NiTi e também o Inconel 625 como metais de adição. No geral, constatou-se que as juntas apresentam comportamento frágil, porém ao se utilizar camada intermediária de Inconel 625 na união entre os metais dissimilares e após tratamento térmico para alívio de tensões, é possível aumentar a resistência mecânica da junta para valores da ordem de 150MPa. As juntas apresentaram uma poça de fusão heterogênea devido a formação de elementos fragilizantes ao longo do metal de solda. Observou-se a formação de uma zona parcialmente diluída (ZPD) correlacionada a um aumento excessivo da dureza nesta região e composição química distinta. / Shape Memory Alloys (SMA) were discovered in the 60s and the development of various systems (NiTi, CuAlNi, CuAlBe, CuZnAl) has been explored since then, with those of the NiTi system the most commonly used. Due to its excellent mechanical properties, good corrosion resistance and biocompatibility, in addition to having the best functional properties of shape memory effect and superelasticity, the NiTi SMA and its ternary variations have become the subject of studies for various applications in different areas. One of the main problems of NiTi SMA is also related to difficulties in forming and machining. For this reason, the welding process can be a good alternative tool to achieve more complex geometry parts, involving the union of NiTi SMA with conventional metals, such as stainless steel. Stainless steel is an important option for union with NiTi SMA, since it also has desired properties of mechanical strength, biocompatibility and corrosion resistance. The union by welding between these two alloys find various barriers, the main one being the formation of brittle intermetallic compounds on the welded joint, limiting its mechanical strength and consistent application. In this context, this study aimed to assess the weldability of thin sheet metal (1 mm thick) of a NiTi SMA with AISI 304 stainless steel (SS) using the micro process GTAW, and study the influence of welding metallurgy in mechanical and metallurgical properties of the joints. The GTAW process was chosen because it is more economical than the usual welding processes for these NiTi alloys such as the laser beam welding (LBW). The NiTi-SS dissimilar joints obtained were characterized by optical microscopy techniques, SEM, EDS, DSC, tensile test to rupture and Vickers hardness. These joints were welded using NiTi SMA and also the Inconel 625 as filler metals. Overall, it was found that the joints have brittle behavior, but when using an intermediate layer of Inconel 625 at the junction between dissimilar metals and after heat treatment for stress relief, it is possible to increase the mechanical strength of the joint for values in the order of 150MPa. The joints exhibited a heterogeneous molten weld pool due to formation of elements along the embrittlement of the weld metal. It was observed the formation of a partially diluted zone (PDZ) correlated to an excessive increase of the hardness in that region and different chemical composition.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1120 |
| Date | 09 July 2018 |
| Creators | OLIVEIRA, Matheus José Cunha de. |
| Contributors | ARAÚJO, Carlos José de., MACIEL, Theóphilo Moura., MELO, João Batista da Costa Agra de., SILVA, Marcos Mesquita da. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds