This thesis presents the results of a series of undrained cyclic triaxial tests carried out on four lime-cement stabilized specimens and clay specimen. The shear resistance degradation rate of lime-cement column subjected to cyclic loading simulated from heavy truck was investigated based on stress-controlled test. The influence of lime and cement on the degradation rate was investigated by comparing the behavior of stabilized kaolin and unstabilized kaolin with similar initial condition. The results indicate an increase in degree of degradation as the number of loading cycles and cyclic strain increase. It is observed that the degradation index has approximately a parabolic relationship with the number of cycles. Generally adding lime and cement to the clay will increase the degradation index which means lower degree of degradation. The degradation parameter, t has a hyperbolic relationship with shear strain, but it loses its hyperbolic shape as the soil getting stronger. On the other hand, for unstabilized clay an approximate linear relationship between degradation index and number of cycles was observed and the degradation parameter has a hyperbolic shape with the increase number of cycles. It was also observed that the stronger the material was, the lesser pore pressure developed in the lime-cement stabilized clay.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-141196 |
Date | January 2014 |
Creators | Gebretsadik, Alex Gezahegn |
Publisher | KTH, Jord- och bergmekanik |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Examensarbete Jord- och bergmekanik, 1652-599X ; 01/14 |
Page generated in 0.0017 seconds