The incorporation of fluorine into SiO2 has been shown to reduce the dielectric constant of the existing materials by reducing the electrical polarizability. However, the incorporation of fluorine has also been shown to decrease film stability. Therefore, new efforts have been made to find different ways to further decrease the relative dielectric constant value of the existing low-k materials. One way to reduce the dielectric constant is by decreasing its density. This reduces the amount of polarizable materials. A good approach is increasing porosity of the film. Recently, fluorinated silica xerogel films have been identified as potential candidates for applications such as interlayer dielectric materials in CMOS technology. In addition to their low dielectric constants, these films present properties such as low refractive indices, low thermal conductivities, and high surface areas. Another approach to lower k is incorporating lighter atoms such as hydrogen or carbon. Silsesquioxane based materials are among them. However, additional integration issues such as damage to these materials caused by plasma etch, plasma ash, and wet etch processes are yet to be overcome. This dissertation reports the effects of triethoxyfluorosilane-based (TEFS) xerogel films when reacted with silylation agents. TEFS films were employed because they form robust silica networks and exhibit low dielectric constants. However, these films readily absorb moisture. Employing silylation reactions enhances film hydrophobicity and permits possible introduction of this film as an interlayer dielectric material. Also, this work describes the effects of SC-CO2 in combination with silylating agents used to functionalize the damaged surface of the ash-damaged MSQ films. Ashed MSQ films exhibit increased water adsorption and dielectric constants due to the carbon depletion and modification of the properties of the low-k material caused by interaction with plasma species. CO2 is widely used as a supercritical solvent, because of its easily accessible critical point, low cost, and non-hazardous nature. Its unique diffusion and surface tension properties make SC-CO2 a good candidate for treatment of porous ultra low-k materials.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc5570 |
| Date | 05 1900 |
| Creators | Orozco-Teran, Rosa Amelia |
| Contributors | Reidy, Richard, Mueller, Dennis, Bouanani, Mohamed El, Gorman, Brian P. |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Use restricted to UNT Community (strictly enforced), Copyright, Orozco-Teran, Rosa Amelia, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0017 seconds