Submitted by Edisangela Bastos (edisangela@ufpa.br) on 2015-02-25T20:22:39Z
No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_DesenvolvimentoProcessosSintese.pdf: 6122919 bytes, checksum: bc93ce91b246da87242f73cc635f738c (MD5) / Approved for entry into archive by Ana Rosa Silva (arosa@ufpa.br) on 2015-02-26T15:24:56Z (GMT) No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_DesenvolvimentoProcessosSintese.pdf: 6122919 bytes, checksum: bc93ce91b246da87242f73cc635f738c (MD5) / Made available in DSpace on 2015-02-26T15:24:56Z (GMT). No. of bitstreams: 2
license_rdf: 22974 bytes, checksum: 99c771d9f0b9c46790009b9874d49253 (MD5)
Dissertacao_DesenvolvimentoProcessosSintese.pdf: 6122919 bytes, checksum: bc93ce91b246da87242f73cc635f738c (MD5)
Previous issue date: 2013 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / No estudo da síntese de Sodalita foram utilizados dois rejeitos de caulins provenientes
de duas empresas de beneficiamento de caulim para cobertura de papel, localizadas na região
Amazônica, que operam na região do Rio Capim (CRC) e do Rio Jari (CRJ). Além desses
rejeitos, também foi utilizado como fonte de alumina e sílica o metacaulim, obtida através da
calcinação dos caulins (MRC e MRJ, respectivamente). Dessa forma, para obter informações
das suas características foram realizadas análises químicas e mineralógicas destes caulins. A
síntese da Sodalita foi realizada variando alguns parâmetros, como material de partida:
partindo-se diretamente de caulim nas temperaturas de 80, 100, 120 e 150 °C; e, partindo-se
de metacaulim na temperatura de 95 °C. Posteriormente, as sínteses foram realizadas
variando-se as soluções básicas a fim de verificar a influencia da presença dos íons OH-, Cl- e
CO32-, bem como a influencia da relação Na2O/Al2O3 na síntese, com a temperatura fixa em
95 ºC para o material de partida MRC. Verificou-se ainda, a influência da temperatura de
síntese variando as em 85, 90 e 95 °C, fixando-se a relação Na2O/Al2O3 na mistura reacional
para determinar as condições ótimas de síntese de Sodalita. Os materiais de partida e os
produtos de síntese foram identificados e caracterizados através de DRX, FRX, MEV,
ATD/TG e EIV. O método de síntese que apresentou melhor resultado foi utilizou o
metacaulim como material de partida, com solução NaOH + Na2CO3 apresentando relação
Na2O/Al2O3 de 3,89 conduzida sob agitação, a 95°C, pressão atmosférica e tempo de 4 horas,
para os dois tipos de caulins (CRC e CRJ). A utilização do metacaulim MRC, a partir do
caulim do Rio Capim, nas condições mencionadas acima obteve-se a conversão de 86,5% em
massa de Sodalita, e o metacaulim MRJ, caulim do Rio Jari, a conversão foi de 73,6% em
sodalita. No que se refere ao tamanho de poros, os produtos partindo de metacaulim tanto do
Rio Capim quanto do Rio Jari foram caracterizados como materiais mesoporosos, porém o
produto partindo de metacaulim do Rio Jari apresentou maior área especifica. / In the study of the Sodalite synthesis used two wastes kaolins from two kaolin
processing industries for paper coating, located in the Amazon region, operating in the region
of Rio Capim (CRC) and Rio Jari (CRJ). Besides this, was also used as a source of silica and
alumina to metakaolin, obtained by calcination of kaolin (MRC and MRJ, respectively).
Preliminary chemical and mineralogical characterization of kaolin was performed to obtain
information of its characteristics. The Sodalite synthesis was performed varying some
parameters, such as starting material: kaolinite was used directly as starting material at
temperatures of 80, 100, 120 and 150 °C, and, starting with metakaolinite at 95 °C. In order to
observe the influence of ions OH, Cl- and CO32-, as well as Na2O/Al2O3 ratio, the syntheses
were carried out varying the basic solutions, set temperature at 95 °C for the starting material
MRC. Furthermore, the Na2O/Al2O3 ratio were maintained constant and temperature were
varied in the reaction mixture to determine the ideal conditions for Sodalite synthesis. The
starting materials and the synthesis products were identified and characterized by using XRay
Diffraction (XRD) and Scanning Electron Microscopy (SEM) analysis, Thermal Methods
(DTA/DTG) and Fourier Transform Infrared Spectrometry (FTIR). The method of synthesis
that show best results were used as starting material metakaolin, with NaOH + Na2CO3
solution having Na2O/Al2O3 ratio of 3.89 conducted under stirring at 95 °C, atmospheric
pressure and a time of 4 hours, for the two types of kaolin (CRC and CRJ). Using the MRC
metakaolin, kaolin from the Rio Capim, under the above conditions was obtained by
conversion of 86.5% by weight of sodalite and MRJ metakaolin, kaolin of the Rio Jari, the
conversion was 73.6% in sodalite. All products were characterized as mesoporous materials,
but starting from the product of metakaolin Rio Jari showed higher specific area.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/6354 |
| Date | 17 January 2013 |
| Creators | SILVA, Liliane Nogueira da |
| Contributors | NEVES, Roberto de Freitas |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Geologia e Geoquímica, UFPA, Brasil, Instituto de Geociências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0105 seconds