Caracterização magnética de nanopartículas de níquel com alto grau de desordem estrutural / Magnetic characterization of nickel nanoparticles with high structural disorder

Orientador: Marcelo Knobel / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Fisica Gleb Wataghin. / Made available in DSpace on 2018-08-12T12:15:41Z (GMT). No. of bitstreams: 1
LeonVanegas_AlvaroAugusto_M.pdf: 1938062 bytes, checksum: c09af0b2555e73ce9f9d903c4094424c (MD5)
Previous issue date: 2008 / Resumo: Neste trabalho estudamos o comportamento magnético de uma amostra de nanopartículas de níquel com alto grau de desordem estrutural com uma distribuição estreita de diâmetros. Encontramos que o sistema apresenta duas fases magnéticas, uma paramagnética, que segue uma lei tipo Curie-Weiss com constante de Curie C = 3, 36 × 10-3emuK/gOe e temperatura crítica de TC = 8, 5 K e outra ferromagnética que não segue o comportamento superparamagnético clássico a altas temperaturas e provavelmente é originada pela formação de pequenos clusters que são os responsáveis pela irreversibilidade observada por baixo dos 23 K nos dados de magnetização FC-ZFC a 50 Oe. Os dados obtidos de Magnetização FC mostram um aumento abrupto da magnetização em 23 K relacionada com o crescimento e criação de novos clusters e estes, devido a interações de tipo dipolar e de troca e a uma forte anisotropia superficial, geram estados frustrados tipo vidro de spin que se refletem na queda na magnetização em 17 K. Em 7 K os restantes spins superficiais que não haviam se incorporado aos clusters ferromagnéticos da partícula tentam-se ordenar. Os dados dos ciclos de histereses confirmam a forte anisotropia superficial e a presença de uma grande porcentagem de spins não ordenados na superfície. / Abstract: We have studied the magnetic behavior of amorphous nickel nanoparticles sample with size narrow distributions. We find that the system have two magnetic phases, one paramagnetic, that follows the Curie-Weiss law with C = 3.36×10-3emuK/gOe and TC= 8.5 K and other ferromagnetic that not follows the classic superparamagnetic behavior to high temperatures and is probably result of small clusters formation, who are the responsibles of observed irreversibility in the Field Cooled magnetization data with magnetic field of 50 Oe. The obtained data of MFC shows a strong increase in the magnetization in 23 K related with the growth and the appearance of new clusters, and these, due to dipolar and exchange interactions and strong surface anisotropy, generates frustrate spin-glass-like states that lead up to a decrease in magnetization at 17 K . At 7 K the system begins to order the remaining superficial spins that are outside the ferromagnetic part of the particle. The histeresis data confirm a strong surface anisotropy and a considerable part of no ordered spins on the surface. / Mestrado / Materiais Magneticos e Propriedades Magneticas / Mestre em Física

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/278269
Date12 August 2018
CreatorsLeon Vanegas, Alvaro Augusto
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Knobel, Marcelo, 1968-, Sinnecker, João Paulo, Schulz, Peter Alexander Bleinroth
Publisher[s.n.], Universidade Estadual de Campinas. Instituto de Física Gleb Wataghin, Programa de Pós-Graduação em Física
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format65 f. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0026 seconds