Orientador: Marcelo Ferraz Mesquita / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T20:29:16Z (GMT). No. of bitstreams: 1
Rodrigues_SabrinaAlessandra_D.pdf: 2058256 bytes, checksum: 25d619422634beb160a254baa71e150a (MD5)
Previous issue date: 2015 / Resumo: O objetivo neste estudo foi avaliar o comportamento de estruturas fundidas em titânio, soldadas à LASER (Light Amplification by Stimulated Emission of Radiation) e à TIG (Tungsten Inert Gas), em relação ao desajuste marginal (bi e tridimensional), força de destorque dos parafusos protéticos, fadiga mecânica, corrosão e tensão induzida aos análogos de mini pilares protéticos. Cinquenta estruturas foram fundidas em titânio comercialmente puro (Ti-cp); vinte infraestruturas (n=20) simulando próteses fixas múltiplas de três elementos; e trinta halteres (n=30). Para cada infraestrutura foram confeccionados dois tipos de index, simulando um desajuste marginal de 200 µm. Um index em gesso especial, para desenvolvimento da análise de tensão, e outro em resina fotoelástica, para avaliação do desajuste marginal (bi e tridimensional), força de destorque, fadiga mecânica e corrosão. Antes e após os procedimentos de soldagem (LASER ou TIG) foram realizadas as seguintes avaliações: mensuração do desajuste marginal, por meio de microscópio óptico (bidimensional) e microtomógrafo de raio-X (tridimensional); análise da tensão induzida aos mini pilares protéticos, por meio da técnica extensométrica; e mensuração da força de destorque dos parafusos protéticos. Os procedimentos de soldagem foram relizados com os seguintes parâmentros: LASER (370/9ms); TIG (36A/60ms). Após a realização dos procedimentos de soldagem (LASER ou TIG) as infraestruturas foram submetidas à ciclagem mecânica ( 280 N/ 106 ciclos /2Hz) para avaliação da força de destorque dos parafusos protéticos pós-ciclagem. A longevidade das estruturas intactas e soldadas (LASER ou TIG) também foi avaliada, por meio de ensaios mecânicos de fadiga, e o comportamento à corrosão, por meio de testes eletroquímicos de espectroscopia de impedância eletroquímica e polarização potenciodinâmica. Os resultados foram analisados estatisticamente (ANOVA fator único/ Teste de Tukey HSD/Teste t de Student/ (?=0,05)). Ambos os procedimentos de soldagem diminuíram o nível de desajuste marginal (bi e tridimensionalmente), aumentaram a intensidade da força de destorque e reduziram a tensão induzida aos mini pilares protéticos. Contudo, após a ciclagem mecânica houve diminuição da intensidade da força de destorque dos parafusos protéicos. As estruturas soldadas à LASER tiveram maior resistência a fadiga, comparada as estruturas soldadas à TIG. O teste de espectroscopia de impedância foi significativo para as infraestruturas soldadas à TIG, comparado com as infraestruturas intactas e soldadas à LASER. Conclui-se que os procedimentos de soldagem tiveram influência sobre a adaptação marginal das infraestruturas, proporcionando maior estabilidade ao sistema implantossuportado. A ciclagem mecânica teve influência sobre a estabilidade dos parafusos protéticos, sendo necessárias proservações periódicas durante o uso da prótese para reaperto e/ou troca dos parafusos. Estruturas fundidas em titânio e soldadas à LASER possuem maior resistência à fadiga do que estruturas soldadas à TIG. Eletroquimicamente, o procedimento de soldagem à LASER possuem melhor comportamento à corrosão comparado ao procedimento de soldagem à TIG / Abstract: The aim of this study was to evaluate titanium casted structures behavior, welded by LASER (Light Amplification by Stimulated Emission of Radiation) and TIG (Tungsten Inert Gas), on marginal misfit (two and three-dimensional), prosthetic screws detorque strength, mechanical fatigue, corrosion and stress induced to the prosthetic mini abutment analogs. Fifty structures were casted in commercially pure titanium (cp-Ti); twenty frameworks (n=20) simulating multiple prostheses of three elements; and thirty dumbbells (n=30). From the frameworks were fabricated two type of index, simulating a marginal misfit of 200µm. One index was fabricated in special plaster to the development of stress analysis, and other in epoxy resin to the development of marginal misfit analysis (two and three-dimensional), detorque strength, mechanical fatigue and corrosion. Before and after welding procedures (LASER or TIG) were developed the following evaluation: marginal misfit analysis, by optical microscope (two-dimensional) and X-ray microtomography (three-dimensional); induced stress analysis on prosthetic mini abutment analogs, by extensometric technique; and measurement of prosthetic screws detorque strength. The welding procedures were made with the following parameters: LASER (370V/9ms); TIG (36A/60ms). After welding procedures (LASER or TIG), the frameworks were submitted to cyclic mechanical (280N; 106 cycles; 2 Hz) by oblique compressive load to evaluation of the detorque strength after the cycling. The longevity of the welded structures was also evaluated by mechanical fatigue testing, and the corrosion behavior by electrochemical tests of electrochemical impedance spectroscopy and potentiodynamic polarization. The results were analyzed statistically (one-way ANOVA / Tukey HSD test / Student-t test (? = 0.05)). Both the welding procedures decreased the marginal misfit level (two and three-dimensionally), increased the detorque strength and decreased of stress induced on prosthetic mini abutment analogs. However, after the mechanical cycling there was decrease of detorque strength of prosthetic screws. The structures welded by LASER had high fatigue resistance than the structures welded by TIG. The impedance spectroscopy test was only significant for frameworks welded by TIG, compared with intact and LASER welded LASER frameworks. It is concluded that welding procedures had influence on marginal fit, providing more stability to the implant-supported system. The mechanical cycling had influence on prosthetic screws stability, being necessary periodic following up to tighten and/or exchange of prosthetic screws. The titanium casted and LASER welded structures were more fatigue resistance than that TIG welded structures. Electroless, LASER welding procedure have better corrosion behavior compared to TIG welding procedure / Doutorado / Protese Dental / Doutora em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289896 |
Date | 27 August 2018 |
Creators | Rodrigues, Sabrina Alessandra, 1986- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mesquita, Marcelo Ferraz, 1967-, Vaz, Luis Geraldo, Rocha, Luís Augusto Sousa Marques da, Consani, Rafael Leonardo Xediek, Barão, Valentim Adelino Ricardo |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 85 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds